Method for modifying synthetic mesoporous crystalline materials

ABSTRACT

This invention relates to a method for modifying a synthetic composition of ultra-large pore crystalline material, e.g., silicate, comprising an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than 18 Angstrom Units and having a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 6.7 kPa (50 torr) and 25° C., by contacting with a treatment composition comprising an inorganic oxide of a trivalent element X, e.g., sodium aluminate, or precursor of said inorganic oxide, under sufficient conditions so that the trivalent element X is incorporated in the crystalline phase material. The composition is suited to use for catalytic conversion of organic compounds or as a sorbent.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of application Ser. No. 07/625,245 (Vartuli et al) filed 10 Dec. 1990, now U.S. Pat. No. 5,098,684 and which in turn is a continuation-in-part of application Ser. No. 07/470,008, filed 25 Jan. 1990, now U.S. Pat. No. 5,102,6 the contents of both being incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a method for modifying compositions of synthetic ultra-large pore crystalline materials, e.g., silicates, by contacting such materials with inorganic oxides of trivalent metals or the precursors of said inorganic oxides.

2. Description of the Prior Art

Porous inorganic solids have found great utility as catalysts and separations media for industrial application. The openness of their microstructure allows molecules access to the relatively large surface areas of these materials that enhance their catalytic and sorptive activity. The porous materials in use today can be sorted into three broad categories using the details of their microstructure as a basis for classification. These categories are the amorphous and paracrystalline supports, the crystalline molecular sieves and modified layered materials. The detailed differences in the microstructures of these materials manifest themselves as important differences in the catalytic and sorptive behavior of the materials, as well as in differences in various observable properties used to characterize them, such as their surface area, the sizes of pores and the variability in those sizes, the presence or absence of X-ray diffraction patterns and the details in such patterns, and the appearance of the materials when their microstructure is studied by transmission electron microscopy and electron diffraction methods.

Amorphous and paracrystalline materials represent an important class of porous inorganic solids that have been used for many years in industrial applications. Typical examples of these materials are the amorphous silicas commonly used in catalyst formulations and the paracrystalline transitional aluminas used as solid acid catalysts and petroleum reforming catalyst supports. The term "amorphous" is used here to indicate a material with no long range order and can be somewhat misleading, since almost all materials are ordered to some degree, at least on the local scale. An alternate term that has been used to describe these materials is "X-ray indifferent". The microstructure of the silicas consists of 100-250 Angstrom particles of dense amorphous silica (Kirk-Othmer Encyclopedia of Chemical Technology, 3rd Edition, Vol. 20, John Wiley & Sons, New York, p. 766-781, 1982), with the porosity resulting from voids between the particles. Since there is no long range order in these materials, the pores tend to be distributed over a rather large range. This lack of order also manifests itself in the X-ray diffraction pattern, which is usually featureless.

Paracrystalline materials such as the transitional aluminas also have a wide distribution of pore sizes, but better defined X-ray diffraction patterns usually consisting of a few broad peaks. The microstructure of these materials consists of tiny crystalline regions of condensed alumina phases and the porosity of the materials results from irregular voids between these regions ( K. Wefers and Chanakya Misra, "Oxides and Hydroxides of Aluminum", Technical Paper No. 19 Revised, Alcoa Research Laboratories, p. 54-59, 1987). Since, in the case of either material, there is no long range order controlling the sizes of pores in the material, the variability in pore size is typically quite high. The sizes of pores in these materials fall into a regime called the mesoporous range, which, for the purposes of this application, is from about 13 to 200 Angstroms.

In sharp contrast to these structurally ill-defined solids are materials whose pore size distribution is very narrow because it is controlled by the precisely repeating crystalline nature of the materials' microstructure. These materials are called "molecular sieves", the most important examples of which are zeolites.

Zeolites, both natural and synthetic, have been demonstrated in the past to have catalytic properties for various types of hydrocarbon conversion. Certain zeolitic materials are ordered, porous crystalline aluminosilicates having a definite crystalline structure as determined by X-ray diffraction, within which there are a large number of smaller cavities which may be interconnected by a number of still smaller channels or pores. These cavities and pores are uniform in size within a specific zeolitic material. Since the dimensions of these pores are such as to accept for adsorption molecules of certain dimensions while rejecting those of larger dimensions, these materials are known as "molecular sieves" and are utilized in a variety of ways to take advantage of these properties.

Such molecular sieves, both natural and synthetic, include a wide variety of positive ion-containing crystalline silicates. These silicates can be described as a rigid three-dimensional framework of SiO₄ and Periodic Table Group IIIB element oxide, e.g. AlO₄, in which the tetrahedra are cross-linked by the sharing of oxygen atoms whereby the ratio of the total Group IIIB element, e.g. aluminum, and Group IVB element, e.g. silicon, atoms to oxygen atoms is 1:2. The electrovalence of the tetrahedra containing the Group IIIB element, e.g. aluminum, is balanced by the inclusion in the crystal of a cation, for example, an alkali metal or an alkaline earth metal cation. This can be expressed wherein the ratio of the Group IIIB element, e.g. aluminum, to the number of various cations, such as Ca/2, Sr/2, Na, K or Li, is equal to unity. One type of cation may be exchanged either entirely or partially with another type of cation utilizing ion exchange techniques in a conventional manner. By means of such cation exchange, it has been possible to vary the properties of a given silicate by suitable selection of the cation. The spaces between the tetrahedra are occupied by molecules of water prior to dehydration.

Prior art techniques have resulted in the formation of a great variety of synthetic zeolites. Many of these zeolites have come to be designated by letter or other convenient symbols, as illustrated by zeolite A (U.S. Pat. No. 2,882,243); zeolite X (U.S. Pat. No. 2,882,244); zeolite Y (U.S. Pat. No. 3,130,007); zeolite ZK-5 (U.S. Pat. No. 3,247,195); zeolite ZK-4 (U.S. Pat. No. 3,314,752); zeolite ZSM-5 (U.S. Pat. No. 3,702,886); zeolite ZSM-11 (U.S. Pat. No. 3,709,979); zeolite ZSM-12 (U.S. Pat. No. 3,832,449); zeolite ZSM-20 (U.S. Pat. No. 3,972,983); ZSM-35 (U.S. Pat. No. 4,016,245); and zeolite ZSM-23 (U.S. Pat. No. 4,076,842), merely to name a few.

The SiO₂ /Al₂ O₃ ratio of a given zeolite is often variable. For example, zeolite X can be synthesized with SiO₂ /Al₂ O₃ ratios of from 2 to 3; zeolite Y, from 3 to about 6. In some zeolites, the upper limit of the SiO₂ /Al₂ O₃ ratio is unbounded. ZSM-5 is one such example wherein the SiO₂ /Al₂ O₃ ratio is at least 5 and up to the limits of present analytical measurement techniques. U.S. Pat. No. 3,941,871 (U.S. Pat. No. Re. 29,948) discloses a porous crystalline silicate made from a reaction mixture containing no deliberately added alumina in the recipe and exhibiting the X-ray diffraction pattern characteristic of ZSM-5. U.S. Pat. Nos. 4,061,724; 4,073,865 and 4,104,294 describe crystalline silicate of varying alumina and metal content.

Aluminum phosphates are taught in U.S. Pat. Nos. 4,310,440 and 4,385,994, for example. These aluminum phosphate materials have essentially electroneutral lattices. U.S. Pat. No. 3,801,704 teaches an aluminum phosphate treated in a certain way to impart acidity.

An early reference to a hydrated aluminum phosphate which is crystalline until heated at about 110° C., at which point it becomes amorphous or transforms, is the "H₁ " phase or hydrate of aluminum phosphate of F.d'Yvoire, Memoir Presented to the Chemical Society, No. 392, "Study of Aluminum Phosphate and Trivalent Iron", Jul 6, 1961 (received), pp. 1762-1776. This material, when crystalline, is identified by the JCPDS International Center for Diffraction Data card number 15-274. Once heated at about 110° C., however, the d'Yvoire material becomes amorphous or transforms to the aluminophosphate form of tridymite.

Compositions comprising crystals having a framework topology after heating at 110° C. or higher giving an X-ray diffraction pattern consistent with a material having pore windows formed by 18 tetrahedral members of about 12-13 Angstroms in diameter are taught in U.S. Pat. No. 4,880,611.

A naturally occurring, highly hydrated basic ferric oxyphosphate mineral, cacoxenite, is reported by Moore and Shen, Nature, Vol. 306, No. 5941, pp. 356-358 (1983) to have a framework structure containing very large channels with a calculated free pore diameter of 14.2 Angstroms. R. Szostak et al., Zeolites: Facts, Fioures, Future, Elsevier Science Publishers B.V., 1989, present work showing cacoxenite as being very hydrophilic, i.e. adsorbing non-polar hydrocarbons only with great difficulty. Their work also shows that thermal treatment of cacoxenite causes an overall decline in X-ray peak intensity.

Silicoaluminophosphates of various structures are taught in U.S. Pat. No. 4,440,871. Aluminosilicates containing phosphorous, i.e. silicoaluminophosphates of particular structures are taught in U.S. Pat. Nos. 3,355,246 (i.e. ZK-21) and 3,791,964 (i.e. ZK-22). Other teachings of silicoaluminophosphates and their synthesis include U.S. Pat. Nos. 4,673,559 (two-phase synthesis method); 4,623,527 (MCM-10); 4,639,358 (MCM-1); 4,647,442 (MCM-2); 4,664,897 (MCM-4); 4,638,357 (MCM-5); and 4,632,811 (MCM-3).

A method for synthesizing crystalline metalloaluminophosphates is shown in U.S. Pat. No. 4,713,227, and an antimonophosphoaluminate and the method for its synthesis are taught in U.S. Pat. No. 4,619,818. U.S. Pat. No. 4,567,029 teaches metalloaluminophosphates, and titaniumaluminophosphate and the method for its synthesis are taught in U.S. Pat. No. 4,500,651.

The phosphorus-substituted zeolites of Canadian Patents 911,416; 911,417; and 911,418 are referred to as "aluminosilicophosphate" zeolites. Some of the phosphorus therein appears to be occluded, not structural.

U.S. Pat. No. 4,363,748 describes a combination of silica and aluminum-calcium-cerium phosphate as a low acid activity catalyst for oxidative dehydrogenation. Great Britain Patent 2,068,253 discloses a combination of silica and aluminum-calcium-tungsten phosphate as a low acid activity catalyst for oxidative dehydrogenation. U.S. Pat. No. 4,228,036 teaches an alumina-aluminum phosphate-silica matrix as an amorphous body to be mixed with zeolite for use as cracking catalyst. U.S. Pat. No. 3,213,035 teaches improving hardness of aluminosilicate catalysts by treatment with phosphoric acid. The catalysts are amorphous.

Other patents teaching aluminum phosphates include U.S. Pat. Nos. 4,365,095; 4,361,705; 4,222,896; 4,210,560; 4,179,358; 4,158,621; 4,071,471; 4,014,945; 3,904,550; and 3,697,550.

The precise crystalline microstructure of most zeolites manifests itself in a well-defined X-ray diffraction pattern that usually contains many sharp maxima and that serves to uniquely define the material. Similarly, the dimensions of pores in these materials are very regular, due to the precise repetition of the crystalline microstructure. All molecular sieves discovered to date have pore sizes in the microporous range, which is usually quoted as 2 to 20 Angstroms, with the largest reported being about 12 Angstroms.

Certain layered materials, which contain layers capable of being spaced apart with a swelling agent, may be pillared to provide materials having a large degree of porosity. Examples of such layered materials include clays. Such clays may be swollen with water, whereby the layers of the clay are spaced apart by water molecules. Other layered materials are not swellable with water, but may be swollen with certain organic swelling agents such as amines and quaternary ammonium compounds. Examples of such non-water swellable layered materials are described in U.S. Pat. No. 4,859,648 and include layered silicates, magadiite, kenyaite, trititanates and perovskites. Another example of a non-water swellable layered material, which can be swollen with certain organic swelling agents, is a vacancy-containing titanometallate material, as described in U.S. Pat. No. 4,831,006.

Once a layered material is swollen, the material may be pillared by interposing a thermally stable substance, such as silica, between the spaced apart layers. The aforementioned U.S. Pat. Nos. 4,831,006 and 4,859,648 describe methods for pillaring the non-water swellable layered materials described therein and are incorporated herein by reference for definition of pillaring and pillared materials.

Other patents teaching pillaring of layered materials and the pillared products include U.S. Pat. Nos. 4,216,188; 4,248,739; 4,176,090; and 4,367,163; and European Patent Application 205,711.

The X-ray diffraction patterns of pillared layered materials can vary considerably, depending on the degree that swelling and pillaring disrupt the otherwise usually well-ordered layered microstructure. The regularity of the microstructure in some pillared layered materials is so badly disrupted that only one peak in the low angle region on the X-ray diffraction pattern is observed, at a d-spacing corresponding to the interlayer repeat in the pillared material. Less disrupted materials may show several peaks in this region that are generally orders of this fundamental repeat. X-ray reflections from the crystalline structure of the layers are also sometimes observed. The pore size distribution in these pillared layered materials is narrower than those in amorphous and paracrystalline materials but broader than that in crystalline framework materials.

SUMMARY OF THE INVENTION

The present invention is directed to a method for modifying a composition of matter comprising an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than 18 Angstrom Units and having a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 6.7 kPa (50 torr) and 25° C. The method comprises contacting the crystalline material, before or after calcination, with a treatment composition comprising an inorganic oxide of a trivalent element X or precursor of said inorganic oxide. Said contacting occurs under sufficient conditions so that the trivalent element X is incorporated in said crystalline phase material.

In a preferred embodiment, the composition of matter comprises an inorganic, porous crystalline phase material having a hexagonal arrangement of uniformly-sized pores at least about 15 Angstroms in diameter and exhibiting, after calcination, a hexagonal electron diffraction pattern that can be indexed with a d₁₀₀ value greater than 18 Angstrom Units.

In another embodiment, a synthetic composition of ultra-large pore crystalline material, e.g., silicate, aluminosilicate, metallosilicate, or metalloaluminosilicate, is modified by contacting such materials with inorganic oxides of trivalent metals. The resulting composition can have an increased trivalent metal content and increased acid activity. The modified composition can also exhibit enhanced thermal and/or hydrothermal stability by virtue of their derivation from a very stable siliceous framework.

Advantageously, the modification can be carried out on the as-synthesized crystalline material without the necessity for removing residual organics. In addition, essentially all internal hydroxyl sites can be functionalized if desired.

DESCRIPTION OF DRAWINGS

FIGS. 1-15 are X-ray diffraction patterns of products of Examples 1-14 and 16, respectively.

FIG. 16 is an isotherm plot of physisorption measurements from Example 22.

FIG. 17 is a plot of physisorption measurements from Example 22 showing pore sizes of various crystalline materials.

FIG. 18 is an electron diffraction pattern of the product of Example 4.

FIG. 19 is a transmission electron micrograph of the product of Example 4.

FIG. 20 is a transmission electron micrograph of the product of Example 5.

FIG. 21 is a transmission electron micrograph of the product of Example 19.

DESCRIPTION OF SPECIFIC EMBODIMENTS

The present invention relates to a method for modifying synthetic ultra large pore composition of matter comprising an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than about 18 Angstrom Units, preferably with a relative intensity of 100%, and having a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 6.7 kPa (50 torr) and 25° C.

In a preferred embodiment, the invention relates to modifying a composition of matter comprising an inorganic, porous crystalline phase material having a hexagonal arrangement of uniformly-sized pores at least 15 Angstrom Units in diameter and exhibiting, after calcination, a hexagonal electron diffraction pattern that can be indexed with a d₁₀₀ value greater than 18 Angstrom Units.

The pore sizes referred to herein are not strict crystallographic dimensions but instead are effective pore sizes determined by sorption measurement. The preferred method of determining pore size employs argon physisorption, which is a known technique and is described in detail in Examples 21(a) and 21(b). In this method the mass of argon adsorbed by a sample at constant temperature but varying relative pressure above the sample is measured and used to plot an adsorption isotherm. The point on the isotherm corresponding to a rapid change of gradient indicates pore filling and can be used to determine pore size by the known mathematical relationships described in Example 21.

The above materials are modified according to the present invention by contacting with a treatment composition comprising an inorganic oxide of a trivalent element X, or a precursor of said inorganic oxide, under conditions sufficient to incorporate the trivalent element X in said crystalline phase material. The trivalent element X is preferably selected from the group consisting of aluminum, boron, iron, gallium and indium.

Examples of suitable sources of inorganic oxides of a trivalent element X include sodium aluminate, sodium gallate, aluminum trichloride, ammonium hexafluoroaluminate, organoaluminum compounds, aluminum alkoxides, gallium trichloride, ammonium hexafluorogallate, organogallium compounds, gallium alkoxides, indium trichloride, ammonium hexafluoroindate, organoindium compounds, indium alkoxides, sodium borate, and boron trifluoride.

The inorganic oxide of the trivalent element can be introduced to the synthetic ultra large pore composition of matter in admixture with an inorganic or organic solvent, e.g. water. The solvent is selected in accordance with the solubility properties of the source of inorganic oxide of the trivalent element X employed. For example, where sodium aluminate is used, water is an effective solvent medium. Generally, the solute and solvent are mixed to provide a solution ranging from 0.1 to 5 molar per trivalent element, preferably 0.5 to 3 molar. The resulting solution is added to the synthetic ultra large pore composition of matter in amounts ranging from 1 to 100 parts of solution to 1 part of synthetic ultra large pore composition of matter, preferably 5 to 20.

As noted above, the solution of inorganic oxide of trivalent element is contacted with the synthetic ultra large pore composition of matter under conditions which suffice to incorporate the trivalent element X in said composition. Suitable conditions include temperatures ranging from 0° to 200° C., preferably 20° to 50° C. and exposure periods ranging from 1 minute to 40 hours, preferably 1 to 20 hours. The treatment is preferably carried out under autogenic pressures.

Synthetic Ultra Large Pore Compositions

The crystalline (i.e. meant here as having sufficient order to provide, after calcination, a diffraction pattern with at least one peak by, for example, X-ray, electron or neutron diffraction) material modified by this invention may be characterized by its heretofore unknown structure, including extremely large pore windows, and high sorption capacity. In general, the material of the invention is "mesoporous", by which is meant that the material has uniform pores of diameter within the range of 13 to 200 Angstrom Units, say, 15 to 200 Angstrom Units. More preferably, the materials of the invention have uniform pores of diameter within the range 18 to 100 Angstrom Units. In this respect, pore size is considered as the maximum perpendicular cross-sectional dimension of the pore.

The material modified by the present invention can be distinguished from other porous inorganic solids by the regularity of its large open pores, whose size more nearly resembles that of amorphous or paracrystalline materials, but whose regular arrangement and uniformity of size (pore size distribution within a single phase of, for example, ±25%, usually ±15% or less of the average pore size of that phase) more closely resemble those of crystalline framework materials such as zeolites.

The composition of matter modified by the present invention comprises an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than 18 Angstrom Units having a relative intensity of 100% and having a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 6.7 kPa (50 torr) and 25° C.

In the preferred arrangement, the porosity of the crystalline material modified by the invention is provided by a generally hexagonal arrangement of open channels, a property that can be readily observed by electron diffraction and transmission electron microscopy. In particular, the transmission electron micrograph of properly oriented specimens of the material show a hexagonal arrangement of large channels and the corresponding electron diffraction pattern gives an approximately hexagonal arrangement of diffraction maxima. The d₁₀₀ spacing of the electron diffraction patterns is the distance between adjacent spots on the hkO projection of the hexagonal lattice and is related to the repeat distance a₀ between channels observed in the electron micrographs through the formula d₁₀₀ =a₀ √3/2. This d₁₀₀ spacing observed in the electron diffraction patterns corresponds to the d-spacing of a low angle peak in the X-ray diffraction pattern of the material. The most highly ordered preparations of the material obtained so far have 20-40 distinct spots observable in the electron diffraction patterns. These patterns can be indexed with the hexagonal hkO subset of unique reflections of 100, 110, 200, 210, etc., and their symmetry-related reflections.

In this respect, it is to be understood that the reference to a hexagonal arrangement of channels is intended to encompass not only mathematically perfect hexagonal symmetry but also an arrangement in which most channels in the material are surrounded by six nearest neighbor channels at substantially the same distance. Defects and imperfections will cause significant numbers of channels to violate this criterion to varying degrees. Samples which exhibit as much as ±25% random deviation from the average repeat distance between adjacent channels still clearly give recognizable images of the present ultra-large pore materials.

The most regular preparations of the preferred material modified by the invention give a hexagonal X-ray diffraction pattern with a few distinct maxima in the extreme low angle region. The X-ray diffraction pattern, however, is not always a sufficient indicator of the presence of these materials, as the degree of regularity in the microstructure and the extent of repetition of the structure within individual particles affect the number of peaks that will be observed. Indeed, preparations with only one distinct peak in the low angle region of the X-ray diffraction pattern have been found to contain substantial amounts of the material of the invention.

In its calcined form, the crystalline material modified by the invention may be further characterized by an X-ray diffraction pattern with at least one peak at a position greater than about 18 Angstrom Units d-spacing (4.909 degrees two-theta for Cu K-alpha radiation) which corresponds to the d₁₀₀ value of the electron diffraction pattern of the material.

More preferably, the calcined crystalline material modified by the invention is characterized by an X-ray diffraction pattern with at least two peaks at positions greater than about 10 Angstrom Units d-spacing (8.842 degrees two-theta for Cu K-alpha radiation), at least one of which is at a position greater than 18 Angstrom Units d-spacing, and no peaks at positions less than 10 Angstrom Units d-spacing with relative intensity greater than about 20% of the strongest peak. Still more particularly, the X-ray diffraction pattern of the calcined material modified by this invention has no peaks at positions less than 10 Angstrom Units d-spacing with relative intensity greater than about 10% of the strongest peak. In the preferred hexagonal arrangement, at least one peak in the X-ray pattern will have a d-spacing corresponding to the d₁₀₀ value of the electron diffraction pattern of the material.

X-ray diffraction data referred to herein were collected on a Scintag PAD X automated diffraction system employing theta-theta geometry, Cu K-alpha radiation, and an energy dispersive X-ray detector. Use of the energy dispersive X-ray detector eliminated the need for incident or diffracted beam monochromators. Both the incident and diffracted X-ray beams were collimated by double slit incident and diffracted collimation systems. The slit sizes used, starting from the X-ray tube source, were 0.5, 1.0, 0.3 and 0.2 mm, respectively. Different slit systems may produce differing intensities for the peaks. The materials of the present invention that have the largest pore sizes may require more highly collimated incident X-ray beams in order to resolve the low angle peak from the transmitted incident X-ray beam.

The diffraction data were recorded by step-scanning at 0.04 degrees of two-theta, where theta is the Bragg angle, and a counting time of 10 seconds for each step. The interplanar spacings, d's, were calculated in Angstrom Units, and the relative intensities of the lines, I/I_(o), where I_(o) is one-hundredth of the intensity of the strongest line, above background, were derived with the use of a profile fitting routine. The intensities were uncorrected for Lorentz and polarization effects. The relative intensities are given in terms of the symbols vs=very strong (75-100), s=strong (50-74), m=medium (25-49) and w=weak (0-24). It should be understood that diffraction data listed as single lines may consist of multiple overlapping lines which under certain conditions, such as very high experimental resolution or crystallographic changes, may appear as resolved or partially resolved lines. Typically, crystallographic changes can include minor changes in unit cell parameters and/or a change in crystal symmetry, without a substantial change in structure. These minor effects, including changes in relative intensities, can also occur as a result of differences in cation content, framework composition, nature and degree of pore filling, thermal and/or hydrothermal history, and peak width/shape variations due to particle size/shape effects, structural disorder or other factors known to those skilled in the art of X-ray diffraction.

The material modified by the invention exhibits an equilibrium benzene adsorption capacity of greater than about 15 grams benzene/100 grams crystal at 6.7 kPa (50 torr) and 25° C. The equilibrium benzene adsorption capacity must, of course, be measured on a sample which exhibits no pore blockage by incidental contaminants. For example, water should be removed by dehydration techniques, e.g. thermal treatment, whereas inorganic amorphous materials, e.g. silica, and organics should be removed by contact with acid or base or other chemical agents and/or physical methods (such as, calcination) so that the detrital material is removed without detrimental effect on the material of the invention.

In general, the crystalline material modified by this invention has a composition, expressed on an anhydrous basis as follows:

    M.sub.n/q (W.sub.a X.sub.b Y.sub.c Z.sub.d O.sub.h)

wherein M is one or more ions, such as, for example, ammonium, Group IA, IIA and VIIB ions, usually hydrogen, sodium and/or fluoride ions; n is the charge of the composition excluding M expressed as oxides; q is the weighted molar average valence of M; n/q is the number of moles or mole fraction of M; W is one or more divalent elements, such as a divalent first row transition metal, e.g. manganese, cobalt, nickel, iron, and/or magnesium, preferably cobalt; X is one or more trivalent elements, such as aluminum, boron, chromium, iron and/or gallium, preferably aluminum; Y is one or more tetravalent elements, such as silicon and/or germanium, preferably silicon; Z is one or more pentavalent elements, such as phosphorus and/or arsenic, preferably phosphorus; a, b, c, and d are mole fractions of W, X, Y, and Z, respectively; (a+b+c+d)=1; and h is a number of from 1 to 2.5. In a preferred embodiment, a=0, d=0 and h=2.

In an even more preferred embodiment, a=0, b=0, d=0 and h=2. Such materials can exhibit relatively high thermal or hydrothermal stability. However, the catalytic activity of such materials, e.g., silicates can be relatively low. Accordingly, the present modification process with an oxide of trivalent element X, can enhance catalytic activity while advantageously affecting thermal or hydrothermal stability.

In the as-synthesized form, the material modified by this invention has a composition, on an anhydrous basis, expressed empirically as follows:

    rRM.sub.n/q (W.sub.a X.sub.b Y.sub.c Z.sub.d O.sub.h)

wherein R is the total organic material used to assist in the synthesis of the material and not included in M as an ion, and r is the coefficient for R, i.e. the number of moles or mole fraction of R.

The M and R components are associated with the material as a result of their presence during crystallization, and are easily removed or, in the case of M, replaced by post-crystallization methods hereinafter more particularly described. For example, the original M, e.g. sodium or chloride, ions of the as-synthesized material of this invention can be replaced by ion exchange with other ions. Preferred replacing ions include metal ions, hydrogen ions, hydrogen precursor, e.g. ammonium, ions and mixtures thereof. Particularly preferred ions are those which tailor the catalytic activity for certain hydrocarbon conversion reactions. These include hydrogen, rare earth metals and metals of Groups IA (e.g. K), IIA (e.g. Ca), VIIA (e.g. Mn), VIIIA (e.g. Ni),IB (e.g. Cu), IIB (e.g. Zn), IIIB (e.g. In), IVB (e.g. Sn), and VIIB (e.g. F) of the Periodic Table of the Elements (Sargent-Welch Scientific Co. Cat. No. S-18806, 1979) and mixtures thereof.

The crystalline (i.e. meant here as having sufficient order to provide a diffraction pattern such as, for example, by X-ray, electron or neutron diffraction, following calcination with at least one peak) mesoporous material modified by this invention may be characterized by its heretofore unknown structure, including extremely large pore windows, and high sorption capacity. The term "mesoporous" is used here to indicate crystals having uniform pores within the range of from about 13 Angstroms to about 200 Angstroms. The materials of this invention will have uniform pores within the range of from about 13 Angstroms to about 200 Angstroms, more usually from about 15 Angstroms to about 100 Angstroms. For the purposes of this application, a working definition of "porous" is a material that adsorbs at least 1 gram of a small molecule, such as Ar, N₂, n-hexane or cyclohexane, per 100 grams of the solid.

The material modified by the present invention can be distinguished from other porous inorganic solids by the regularity of its large open pores, whose pore size more nearly resembles that of amorphous or paracrystalline materials, but whose regular arrangement and uniformity of size (pore size distribution within a single phase of, for example, ±25%, usually ±15% or less of the average pore size of that phase) resemble more those of crystalline framework materials such as zeolites. The material appears to have a hexagonal arrangement of large open channels that can be synthesized with open internal diameters from about 13 Angstroms to about 200 Angstroms. The term "hexagonal" is intended to encompass not only materials that exhibit mathematically perfect hexagonal symmetry within the limits of experimental measurement, but also those with significant observable deviations from that ideal state. A working definition as applied to the microstructure of the present invention would be that most channels in the material would be surrounded by six nearest neighbor channels at roughly the same distance. Defects and imperfections will cause significant numbers of channels to violate this criterion to varying degrees, depending on the quality of the material's preparation. Samples which exhibit as much as ±25% random deviation from the average repeat distance between adjacent channels still clearly give recognizable images of the present ultra-large pore materials. Comparable variations are also observed in the d₁₀₀ values from the electron diffraction patterns. Transmission electron micrographs of materials within this working definition are shown in FIGS. 19, 20, and 21.

The most regular preparations of the material modified by the present invention give an X-ray diffraction pattern with a few distinct maxima in the extreme low angle region. The positions of these peaks approximately fit the positions of the hkO reflections from a hexagonal lattice. The X-ray diffraction pattern, however, is not always a sufficient indicator of the presence of these materials, as the degree of regularity in the microstructure and the extent of repetition of the structure within individual particles affect the number of peaks that will be observed. Indeed, preparations with only one distinct peak in the low angle region of the X-ray diffraction pattern have been found to contain substantial amounts of the material in them. Other techniques to illustrate the microstructure of this material are transmission electron microscopy and electron diffraction. Properly oriented specimens of the material show a hexagonal arrangement of large channels and the corresponding electron diffraction pattern gives an approximately hexagonal arrangement of diffraction maxima. The d₁₀₀ spacing of the electron diffraction patterns is the distance between adjacent spots on the hkO projection of the hexagonal lattice and is related to the repeat distance a₀ between channels observed in the electron micrographs through the formula d₁₀₀ =a₀ √3/2. This d₁₀₀ spacing observed in the electron diffraction patterns corresponds to the d-spacing of a low angle peak in the X-ray diffraction pattern of the material. The most highly ordered preparations of the material obtained so far have 20-40 distinct spots observable in the electron diffraction patterns. These patterns can be indexed with the hexagonal hkO subset of unique reflections of 100, 110, 200, 210, etc., and their symmetry-related reflections.

In its calcined form, the crystalline material modified by the invention may be further characterized by an X-ray diffraction pattern with at least one peak at a position greater than about 18 Angstrom Units d-spacing (4.909 degrees two-theta for Cu K-alpha radiation) which corresponds to the d₁₀₀ value of the electron diffraction pattern of the material, and an equilibrium benzene adsorption capacity of greater than about 15 grams benzene/100 grams crystal at 50 torr and 25° C. (basis: crystal material having been treated in an attempt to insure no pore blockage by incidental contaminants, if necessary).

The equilibrium benzene adsorption capacity characteristic of this material is measured on the basis of no pore blockage by incidental contaminants. For instance, the sorption test will be conducted on the crystalline material phase having any pore blockage contaminants and water removed by ordinary methods. Water may be removed by dehydration techniques, e.g. thermal treatment. Pore blocking inorganic amorphous materials, e.g. silica, and organics may be removed by contact with acid or base or other chemical agents such that the detrital material will be removed without detrimental effect on the crystal of the invention.

More particularly, the calcined crystalline non-layered material modified by the invention may be characterized by an X-ray diffraction pattern with at least two peaks at positions greater than about 10 Angstrom Units d-spacing (8.84 degrees two-theta for Cu K-alpha radiation), at least one of which is at a position greater than about 18 Angstrom Units d-spacing, and no peaks at positions less than about 10 Angstrom units d-spacing with relative intensity greater than about 20% of the strongest peak. Still more particularly, the X-ray diffraction pattern of the calcined material will have no peaks at positions less than about 10 Angstrom units d-spacing with relative intensity greater than about 10% of the strongest peak. In any event, at least one peak in the X-ray diffraction pattern will have a d-spacing that corresponds to the d₁₀₀ value of the electron diffraction pattern of the material.

Still more particularly, the calcined inorganic, non-layered crystalline material modified by the invention is characterized as having a pore size of about 13 Angstroms or greater, preferably 15 Angstroms or greater, as measured by physisorption measurements, hereinafter more particularly set forth. Pore size is considered a maximum perpendicular cross-section pore dimension of the crystal.

X-ray diffraction data were collected on a Scintag PAD X automated diffraction system employing theta-theta geometry, Cu K-alpha radiation, and an energy dispersive X-ray detector. Use of the energy dispersive X-ray detector eliminated the need for incident or diffracted beam monochromators. Both the incident and diffracted X-ray beams were collimated by double slit incident and diffracted collimation systems. The slit sizes used, starting from the X-ray tube source, were 0.5, 1.0, 0.3 and 0.2 mm, respectively. Different slit systems may produce differing intensities for the peaks. The materials of the present invention that have the largest pore sizes may require more highly collimated incident X-ray beams in order to resolve the low angle peak from the transmitted incident X-ray beam.

The diffraction data were recorded by step-scanning at 0.04 degrees of two-theta, where theta is the Bragg angle, and a counting time of 10 seconds for each step. The interplanar spacings, d's, were calculated in Angstrom units (A), and the relative intensities of the lines, I/I_(o), where I_(o) is one-hundredth of the intensity of the strongest line, above background, were derived with the use of a profile fitting routine. The intensities were uncorrected for Lorentz and polarization effects. The relative intensities are given in terms of the symbols vs=very strong (75-100), s=strong (50-74), m=medium (25-49) and w=weak (0-24). It should be understood that diffraction data listed as single lines may consist of multiple overlapping lines which under certain conditions, such as very high experimental resolution or crystallographic changes, may appear as resolved or partially resolved lines. Typically, crystallographic changes can include minor changes in unit cell parameters and/or a change in crystal symmetry, without a substantial change in structure. These minor effects, including changes in relative intensities, can also occur as a result of differences in cation content, framework composition, nature and degree of pore filling, thermal and/or hydrothermal history, and peak width/shape variations due to particle size/shape effects, structural disorder or other factors known to those skilled in the art of X-ray diffraction.

The equilibrium benzene adsorption capacity is determined by contacting the material of the invention, after dehydration or calcination at, for example, about 540° C. for at least about one hour and other treatment, if necessary, in an attempt to remove any pore blocking contaminants, at 25° C. and 50 torr benzene until equilibrium is reached. The weight of benzene sorbed is then determined as more particularly described hereinafter.

When used as a sorbent or catalyst component, the composition modified by the invention should be subjected to treatment to remove part or all of any organic constituent. The present composition can also be used as a catalyst component in intimate combination with a hydrogenating component such as tungsten, vanadium, molybdenum, rhenium, nickel, cobalt, chromium, manganese, or a noble metal such as platinum or palladium or mixtures thereof where a hydrogenation-dehydrogenation function is to be performed. Such component can be in the composition by way of co-crystallization, exchanged into the composition to the extent a Group IIIB element, e.g. aluminum, is in the structure, impregnated therein or intimately physically admixed therewith. Such component can be impregnated in or on to it such as, for example, by, in the case of platinum, treating the silicate with a solution containing a platinum metal-containing ion. Thus, suitable platinum compounds for this purpose include chloroplatinic acid, platinous chloride and various compounds containing the platinum amine complex.

The above crystalline material, especially in its metal, hydrogen and ammonium forms can be beneficially converted to another form by thermal treatment (calcination). This thermal treatment is generally performed by heating one of these forms at a temperature of at least 400° C. for at least 1 minute and generally not longer than 20 hours, preferably from about 1 to about 10 hours. While subatmospheric pressure can be employed for the thermal treatment, atmospheric pressure is desired for reasons of convenience, such as in air, nitrogen, ammonia, etc. The thermal treatment can be performed at a temperature up to about 750° C. The thermally treated product is particularly useful in the catalysis of certain hydrocarbon conversion reactions.

The crystalline material modified by this invention, when employed either as an adsorbent or as a catalyst component in an organic compound conversion process should be dehydrated, at least partially. This can be done by heating to a temperature in the range of 200° C. to 595° C. in an atmosphere such as air, nitrogen, etc. and at atmospheric, subatmospheric or superatmospheric pressures for between 30 minutes and 48 hours. Dehydration can also be performed at room temperature merely by placing the composition in a vacuum, but a longer time is required to obtain a sufficient amount of dehydration.

The crystalline material can be prepared by one of several methods, each with particular limitations.

A first method involves a reaction mixture having an X₂ O₃ /YO₂ mole ratio of from 0 to about 0.5, but an Al₂ O₃ /SiO₂ mole ratio of from 0 to 0.01, a crystallization temperature of from about 25° C. to about 250° C., preferably from about 50° C. to about 175° C., and an organic directing agent, hereinafter more particularly described, or, preferably a combination of that organic directing agent plus an additional organic directing agent, hereinafter more particularly described. This first method comprises preparing a reaction mixture containing sources of, for example, alkali or alkaline earth metal (M), e.g. sodium or potassium, cation if desired, one or a combination of oxides selected from the group consisting of divalent element W, e.g. cobalt, trivalent element X, e.g. aluminum, tetravalent element Y, e.g. silicon, and pentavalent element Z, e.g. phosphorus, an organic (R) directing agent, hereinafter more particularly described, and a solvent or solvent mixture, such as, for example, C₁ -C₆ alcohols, C₁ -C₆ diols and/or water, especially water, said reaction mixture having a composition, in terms of mole ratios of oxides, within the following ranges:

    ______________________________________                                         Reactants         Useful     Preferred                                         ______________________________________                                         X.sub.2 O.sub.3 /YO.sub.2                                                                        0 to    0.5    0.001 to                                                                              0.5                                    Al.sub.2 O.sub.3 /SiO.sub.2                                                                      0 to    0.01   0.001 to                                                                              0.01                                   X.sub.2 O.sub.3 /(YO.sub.2 + Z.sub.2 O.sub.5)                                                    0.1 to  100    0.1 to 20                                     X.sub.2 O.sub.3 /(YO.sub.2 + WO + Z.sub.2 O.sub.5)                                               0.1 to  100    0.1 to 20                                     Solvent/          1 to    1500   5 to   1000                                   (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3)                            OH.sup.- /YO.sub.2                                                                               0 to    10     0 to   5                                      (M.sub.2/e O + R.sub.2/f O)/                                                                     0.01 to 20     0.05 to                                                                               5                                      (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3)                            M.sub.2/e O/      0 to    10     0 to   5                                      (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3)                            R.sub.2/f O/      0.01 to 2.0    0.03 to                                                                               1.0                                    (YO.sub.2 + WO + Z.sub. 2 O.sub.5 + X.sub.2 O.sub.3)                           ______________________________________                                    

wherein e and f are the weighted average valences of M and R, respectively.

In this first method, when no Z and/or W oxides are added to the reaction mixture, the pH is important and must be maintained at from about 9 to about 14. When Z and/or W oxides are present in the reaction mixture, the pH is not narrowly important for synthesis of the present crystalline material. In this, as well as the following methods for synthesis of the present material the R_(2/f) O/(YO₂ +WO+Z₂ O₅ +X₂ O₃) ratio is important. When this ratio is less than 0.01 or greater than 2.0, impurity products tend to be synthesized at the expense of the present material.

A second method for synthesis of the present crystalline material involves a reaction mixture having an X₂ O₃ /YO₂ mole ratio of from about 0 to about 0.5, a crystallization temperature of from about 25° C. to about 250° C., preferably from about 50° C. to about 175° C., and two separate organic directing agents, i.e. the organic and additional organic directing agents, hereinafter more particularly described. This second method comprises preparing a reaction mixture containing sources of, for example, alkali or alkaline earth metal (M), e.g. sodium or potassium, cation if desired, one or a combination of oxides selected from the group consisting of divalent element W, e.g. cobalt, trivalent element X, e.g. aluminum, tetravalent element Y, e.g. silicon, and pentavalent element Z, e.g. phosphorus, a combination of organic directing agent and additional organic directing agent (R), each hereinafter more particularly described, and a solvent or solvent mixture, such as, for example, C₁ -C₆ alcohols, C₁ -C₆ diols and/or water, especially water, said reaction mixture having a composition, in terms of mole ratios of oxides, within the following ranges:

    ______________________________________                                         Reactants         Useful     Preferred                                         ______________________________________                                         X.sub.2 O.sub.3 /YO.sub.2                                                                        0 to    0.5    0.001 to                                                                              0.5                                    X.sub.2 O.sub.3 /(YO.sub.2 + Z.sub.2 O.sub.5)                                                    0.1 to  100    0.1 to 20                                     X.sub.2 O.sub.3 /(YO.sub.2 + WO + Z.sub.2 O.sub.5)                                               0.1 to  100    0.1 to 20                                     Solvent/          1 to    1500   5 to   1000                                   (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3)                            OH.sup.- /YO.sub.2                                                                               0 to    10     0 to   5                                      (M.sub.2/e O + R.sub.2/f O)/                                                                     0.01 to 20     0.05 to                                                                               5                                      (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3)                            M.sub.2/e O/      0 to    10     0 to   5                                      (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3)                            R.sub.2/f O/      0.1 to  2.0    0.12 to                                                                               1.0                                    (YO.sub.2 + WO + Z.sub.2 O.sub.5 + X.sub.2 O.sub.3 )                           ______________________________________                                    

wherein e and f are the weighted average valences of M and R, respectively.

In this second method, when no Z and/or W oxides are added to the reaction mixture, the pH is important and must be maintained at from about 9 to about 14. When Z and/or W oxides are present in the reaction mixture, the pH is not narrowly important for crystallization of the present invention.

A third method for synthesis of the present crystalline material is where X comprises aluminum and Y comprises silicon, the crystallization temperature must be from about 25° C. to about 175° C., preferably from about 50° C. to about 150° C., and an organic directing agent, hereinafter more particularly described, or, preferably a combination of that organic directing agent plus an additional organic agent, hereinafter more particularly described, is used. This third method comprises preparing a reaction mixture containing sources of, for example, alkali or alkaline earth metal (M), e.g. sodium or potassium, cation if desired, one or more sources of aluminum and/or silicon, an organic (R) directing agent, hereinafter more particularly described, and a solvent or solvent mixture, such as, for example C₁ -C₆ alcohols, C₁ -C₆ diols and/or water, especially water, said reaction mixture having a composition, in terms of mole ratios of oxides, within the following ranges:

    ______________________________________                                         Reactants     Useful     Preferred                                             ______________________________________                                         Al.sub.2 O.sub.3 /SiO.sub.2                                                                  0 to    0.5    0.001 to 0.5                                      Solvent/SiO.sub.2                                                                            1 to    1500   5 to     1000                                     OH.sup.- /SiO.sub.2                                                                          0 to    10     0 to     5                                        (M.sub.2/e O + R.sub.2/f O)/                                                                 0.01 to 20     0.05 to  5                                        (SiO.sub.2 + Al.sub.2 O.sub.3)                                                 M.sub.2/e O/  0 to    5      0 to     3                                        (SiO.sub.2 + Al.sub.2 O.sub.3)                                                 R.sub.2/f O/  0.01 to 2      0.03 to  1                                        (SiO.sub.2 + Al.sub.2 O.sub.3)                                                 ______________________________________                                    

wherein e and f are the weighted average valences of M and R, respectively.

In this third method, the pH is important and must be maintained at from about 9 to about 14. This method involves the following steps:

(1) Mix the organic (R) directing agent with the solvent or solvent mixture such that the mole ratio of solvent/R_(2/f) O is within the range of from about 50 to about 800, preferably from about 50 to 500. This mixture constitutes the "primary template" for the synthesis method.

(2) To the primary template mixture of step (1) add the sources of oxides, e.g. silica and/or alumina such that the ratio of R_(2/f) O(SiO₂ +Al₂ O₃) is within the range of from about 0.01 to about 2.0.

(3) Agitate the mixture resulting from step (2) at a temperature of from about 20° C. to about 40° C., preferably for from about 5 minutes to about 3 hours.

(4) Allow the mixture to stand with or without agitation, preferably at a temperature of from about 20° C. to about 100° C., and preferably for from about 10 minutes to about 24 hours.

(5) Crystallize the product from step (4) at a temperature of from about 50° C. to about 175° C., preferably for from about 1 hour to about 72 hours. Crystallization temperatures higher in the given ranges are most preferred.

A fourth method for the present synthesis involves the reaction mixture used for the third method, but the following specific procedure with tetraethylorthosilicate the source of silicon oxide:

(1) Mix the organic (R) directing agent with the solvent or solvent mixture such that the mole ratio of solvent/R_(2/f) O is within the range of from about 50 to about 800, preferably from about 50 to 500. This mixture constitutes the "primary template" for the synthesis method.

(2) Mix the primary template mixture of step (1) with tetraethylorthosilicate and a source of aluminum oxide, if desired, such that the R_(2/f) O/SiO₂ mole ratio is in the range of from about 0.5 to about 2.0.

(3) Agitate the mixture resulting from step (2) for from about 10 minutes to about 6 hours, preferably from about 30 minutes to about 2 hours, at a temperature of from about 0° C. to about 25° C., and a pH of less than 12. This step permits hydrolysis/polymerization to take place and the resultant mixture will appear cloudy.

(4) Crystallize the product from step (3) at a temperature of from about 25° C. to about 150° C., preferably from about 95° C. to about 110° C., for from about 4 to about 72 hours, preferably from about 16 to about 48 hours.

In each of the above methods, batch crystallization of the present crystalline material can be carried out under either static or agitated, e.g. stirred, conditions in a suitable reactor vessel, such as for example, polypropylene jars or teflon lined or stainless steel autoclaves. Crystallization may also be conducted continuously in suitable equipment. The total useful range of temperatures for crystallization is noted above for each method for a time sufficient for crystallization to occur at the temperature used, e.g. from about 5 minutes to about 14 days. Thereafter, the crystals are separated from the liquid and recovered.

When a source of silicon is used in the synthesis method, it is preferred to use at least in part an organic silicate, such as, for example, a quaternary ammonium silicate. Non-limiting examples of such a silicate include tetramethylammonium silicate and tetraethylorthosilicate.

By adjusting conditions of the synthesis reaction for each method, like temperature, pH and time of reaction, etc., within the above limits, embodiments of the present non-layered crystalline material with a desired average pore size may be prepared. In particular, changing the pH, the temperature or the reaction time may promote formation of product crystals with different average pore size.

Non-limiting examples of various combinations of W, X, Y and Z contemplated for the first and second synthesis methods include:

    ______________________________________                                         W       X               Y     Z                                                ______________________________________                                         --      Al              Si    --                                               --      Al              --    P                                                --      Al              Si    P                                                Co      Al              --    P                                                Co      Al              Si    P                                                --      --              Si    --                                               ______________________________________                                    

including the combinations of W being Mg, or an element selected from the divalent first row transition metals, e.g. Mn, Co and Fe; X being B, Ga or Fe; and Y being Ge.

An organic directing agent for use in each of the above methods for synthesizing the present material from the respective reaction mixtures is an ammonium or phosphonium ion of the formula R₁ R₂ R₃ R₄ Q⁺, i.e.: ##STR1## wherein Q is nitrogen or phosphorus and wherein at least one of R₁, R₂, R₃ and R₄ is aryl or alkyl of from 6 to about 36 carbon atoms, e.g. --C₆ H₁₃, --C₁₀ H₂₁, --C₁₆ H₃₃ and --C₁₈ H₃₇, or combinations thereof, the remainder of R₁, R₂, R₃ and R₄ being selected from the group consisting of hydrogen, alkyl of from 1 to 5 carbon atoms and combinations thereof. The compound from which the above ammonium or phosphonium ion is derived may be, for example, the hydroxide, halide, silicate, or mixtures thereof.

In the first and third methods above it is preferred to have an additional organic directing agent and in the second method it is required to have a combination of the above organic directing agent and an additional organic directing agent. That additional organic directing agent is the ammonium or phosphonium ion of the above directing agent formula wherein R₁, R₂, R₃ and R₄ together or separately are selected from the group consisting of hydrogen and alkyl of 1 to 5 carbon atoms and combinations thereof. Any such combination of organic directing agents go to make up "R" and will be in molar ratio of about 100/1 to about 0.01/1, first above listed organic directing agent/additional organic directing agent.

The particular effectiveness of the presently required directing agent, when compared with other such agents known to direct synthesis of one or more other crystal structures, is believed due to its ability to function as a template in the above reaction mixture in the nucleation and growth of the desired ultra-large pore crystals with the limitations discussed above. Non-limiting examples of these directing agents include cetyltrimethylammonium, cetyltrimethylphosphonium, octadecyltrimethylphosphonium, cetylpyridinium, myristyltrimethylammonium, decyltrimethylammonium, dodecyltrimethylammonium and dimethyldidodecylammonium.

It should be realized that the reaction mixture components can be supplied by more than one source. The reaction mixture can be prepared either batchwise or continuously. Crystal size and crystallization time of the new crystalline material will vary with the nature of the reaction mixture employed and the crystallization conditions.

The crystals prepared by the instant invention can be shaped into a wide variety of particle sizes. Generally speaking, the particles can be in the form of a powder, a granule, or a molded product, such as an extrudate having particle size sufficient to pass through a 2 mesh (Tyler) screen and be retained on a 400 mesh (Tyler) screen. In cases where the catalyst is molded, such as by extrusion, the crystals can be extruded before drying or partially dried and then extruded.

The present compositions are useful as catalyst components for catalyzing the conversion of organic compounds, e.g. oxygenates and hydrocarbons, by acid-catalyzed reactions. The size of the pores is also such that the spatiospecific selectivity with respect to transition stat species is minimized in reactions such as cracking (Chen et al., "Shape Selective Catalysis in Industrial Applications", 36 CHEMICAL INDUSTRIES, pgs. 41-61 (1989) to which reference is made for a discussion of the factors affecting shape selectivity). Diffusional limitations are also minimized as a result of the very large pores in the present materials. For these reasons, the present compositions are especially useful for catalyzing reactions which occur in the presence of acidic sites on the surface of the catalyst and which involve reactants, products or transitional state species which have large molecular sizes, too great for undergoing similar reactions with conventional large pore size solid catalysts, for example, large pore size zeolites such as zeolite X, Y, L, ZSM-4, ZSM-18, and ZSM-20.

Thus, the present catalytic compositions will catalyze reactions such as cracking, and hydrocracking, and other conversion reactions using hydrocarbon feeds of varying molecular sizes, but with particular applicability to feeds with large molecular sizes such as highly aromatic hydrocarbons with substituted or unsubstituted polycyclic aromatic components, bulky naphthenic compounds or highly substituted compounds with bulky steric configurations, e.g. molecular sizes of about 13 Angstroms or more. The present catalytic compositions are particularly useful for reactions in which the molecular weight of the feed is reduced to a lower value, i.e. to reactions involving cracking such as cracking or hydrocracking. Cracking may be conducted at a temperature of from about 200° C. to about 800° C., a pressure of from about atmospheric to about 100 psig and contact time of from about 0.1 second to about 60 minutes. Hydrocracking may be conducted at a temperature of from about 150° C. to about 550° C., a pressure of from about 100 psig to about 3000 psig, and a weight hourly space velocity of from about 0.1 hr⁻¹ to about 100 hr⁻¹, with a hydrogen/hydrocarbon molar ratio of from about 0.1 to about 100.

The catalytic compositions of matter according to the present invention may also be used for selective conversion of inorganic compounds such as oxides of nitrogen in mixtures of gases which contain nitrogen oxides (NO_(x)), for example, industrial exhaust gases and the gases formed during the oxidative regeneration of catalysts used in the processing of hydrocarbons, especialy in catalytic cracking operations. The porous crystalline material may be used in a matrixed or unmatrixed form for this purpose and may suitably be formed into extrudates, pellets or other shapes to permit the passage of gases over the catalyst with the minimum pressure drop. The crystalline material is preferably at least partly in the hydrogen form, but it may advantageously contain a minor amount of a noble metal as a catalytic component, especially a metal of Periods 5 and 6 of Group VIIIA of the Periodic Table, especially platinum, palladium, ruthenium, rhodium, iridium or mixtures thereof. Amounts of noble metal up to about 1 weight percent are typical with lower amounts, e.g. up to about 0.1 or 0.5 weight percent being preferred.

The NO_(x) reduction is suitably conducted by passing the gas containing the oxides of nitrogen over the catalyst at an elevated temperature, typically at least 200° C., and usually within the range of 200° to 600° C. The gas mixture may be mixed with ammonia to promote reduction of the oxides of nitrogen and pre-mixing may be conducted at a temperature of up to about 200° C. The amount of ammonia which is mixed with the gas mixture is typically within the range of 0.75 to 1.25 the stoichiometric amount, which itself varies according to the ratio of the different oxides of nitrogen in the gas mixture, as shown by the equations:

    6NO.sub.2 +8NH.sub.3 =7N.sub.2 +12H.sub.2 O

    6NO+4NH.sub.3 =5N.sub.2 +6H.sub.2 O

The crystalline catalytic compositions of matter may also be used for the reduction of oxides of nitrogen in gaseous mixtures in the presence of other reducing agents such as carbon or carbon monoxide. Reduction of the oxides of nitrogen in this way is of particular utility in the regeneration of fluid catalytic cracking (FCC) catalysts, since regeneration under appropriate conditions will produce the required concentrations of carbon monoxide which may then be used to reduce the proportion of NO_(x) in the regeneration gases in the presence of the catalyst.

Because the present catalytic compositions have been found to be stable, their use as cracking catalysts, e.g. in fluid catalytic cracking processes, with resid feeds will represent an especially favorable mode of utilization. Still further, they may be used in combination with one or more other catalyst components such as, for example, cracking catalysts comprising silica-alumina and/or zeolite Y, e.g. USY.

The present catalytic compositions are especially useful for reactions using high molecular weight, high boiling or non-distillable feeds, especially residual feeds, i.e. feeds which are essentially non-distillable or feeds which have an initial boiling point (5% point) above about 1050° F. Residual feeds which may be used with the present catalytic compositions include feeds with API gravities below about 20, usually below 15 and typically from 5 to 10 with Conradson Carbon Content (CCR) of at least 1% by weight and more usually at least 5% or more, e.g. 5-10%. In some resid fractions the CCR may be as high as about 20 weight percent or even higher. The aromatic contents of these feeds will be correspondingly high, as may the contents of heteroatoms such as sulfur and nitrogen, as well as metals. Aromatics content of these feeds will usually be at least 50 weight percent and typically much higher, usually at least 70 or 80 weight percent, with the balance being principally naphthenes and heterocyclics. Typical petroleum refinery feeds of this type include atmospheric and vacuum tower resids, asphalts, aromatic extracts from solvent extraction processes, e.g. phenol or furfural extraction, deasphalted oils, slop oils and residual fractions from various processes such as lube production, coking and the like. High boiling fractions with which the present catalytic compositions may be used include gas oils, such as atmospheric gas oils; vacuum gas oils; cycle oils, especially heavy cycle oil; deasphalted oils; solvent extracts, such as bright stock; heavy gas oils, such as coker heavy gas oils; and the like. The present catalytic materials may also be utilized with feeds of non-petroleum origin, for example, synthetic oils produced by coal liquefaction, Fischer-Tropsch waxes and heavy fractions and other similar materials.

The compositions of this invention can also be used as adsorbents and separation vehicles in pharmaceutical and fine chemical applications. For example, these ultra-large pore compositions may be used in the purification of drugs like insulin or be used as solid vehicles for the controlled delivery of drugs. Another application for use of these ultra-large pore materials involves waste disposal where the extraordinary pore volumes are exploited. Therefore, at least one component can be partially or substantially totally separated from a mixture of components having differential sorption characteristics with respect to the present ultra-large pore composition by contacting the mixture with the composition to selectively sorb the one component. Examples of this include contacting a mixture comprising water and at least one hydrocarbon component, whereby the at least one hydrocarbon component is selectively sorbed. Another example includes selective sorption of at least one hydrocarbon component from a mixture comprising same and at least one additional hydrocarbon component.

As in the case of many catalysts, it may be desired to incorporate the new crystal composition with another material resistant to the temperatures and other conditions employed in organic conversion processes. Such materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and/or metal oxides such as alumina, titania and/or zirconia. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the new crystal, i.e. combined therewith or present during synthesis of the new crystal, which is active, tends to change the conversion and/or selectivity of the catalyst in certain organic conversion processes. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate of reaction. These materials may be incorporated with naturally occurring clays, e.g. bentonite and kaolin, to improve the crush strength of the catalyst under commercial operating conditions. Said materials, i.e. clays, oxides, etc., function as binders for the catalyst. It is desirable to provide a catalyst having good crush strength because in commercial use it is desirable to prevent the catalyst from breaking down into powder-like materials. These clay binders have been employed normally only for the purpose of improving the crush strength of the catalyst.

Naturally occurring clays which can be composited with the new crystal include the montmorillonite and kaolin family, which families include the subbentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite, or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification.

In addition to the foregoing materials, the new crystal can be composited with a porous matrix material such as silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia.

It may be desirable to provide at least a part of the foregoing matrix materials in colloidal form so as to facilitate extrusion of the bound catalyst component(s).

The relative proportions of finely divided crystalline material and inorganic oxide matrix vary widely, with the crystal content ranging from about 1 to about 90 percent by weight and more usually, particularly when the composite is prepared in the form of beads, in the range of about 2 to about 80 weight percent of the composite.

In order to more fully illustrate the nature of the invention and the manner of practicing same, the following examples are presented.

In the examples, whenever sorption data are set forth for comparison of sorptive capacities for water, cyclohexane, benzene and/or n-hexane, they are Equilibrium Adsorption values determined as follows:

A weighed sample of the adsorbent, after calcination at about 540° C. for at least about 1 hour and other treatment, if necessary, to remove any pore blocking contaminants, is contacted with the desired pure adsorbate vapor in an adsorption chamber. The increase in weight of the adsorbent is calculated as the adsorption capacity of the sample in terms of grams/100 grams adsorbent based on adsorbent weight after calcination at about 540° C. The present composition exhibits an equilibrium benzene adsorption capacity at 50 Torr and 25° C. of greater than about 15 grams/100 grams, particularly greater than about 17.5 g/100 g/ and more particularly greater than about 20 g/100 g.

A preferred way to do this is to contact the desired pure adsorbate vapor in an adsorption chamber evacuated to less than 1 mm at conditions of 12 Torr of water vapor, 40 Torr of n-hexane or cyclohexane vapor, or 50 Torr of benzene vapor, at 25° C. The pressure is kept constant (within about ±0.5 mm) by addition of adsorbate vapor controlled by a manostat during the adsorption period. As adsorbate is adsorbed by the new crystal, the decrease in pressure causes the manostat to open a valve which admits more adsorbate vapor to the chamber to restore the above control pressures. Sorption is complete when the pressure change is not sufficient to activate the manostat.

Another way of doing this for benzene adsorption data is on a suitable thermogravimetric analysis system, such as a computer-controlled 990/951 duPont TGA system. The adsorbent sample is dehydrated (physically sorbed water removed) by heating at, for example, about 350° C. or 500° C. to constant weight in flowing helium. If the sample is in as-synthesized form, e.g. containing organic directing agents, it is calcined at about 540° C. in air and held to constant weight instead of the previously described 350° C. or 500° C. treatment. Benzene adsorption isotherms are measured at 25° C. by blending a benzene saturated helium gas stream with a pure helium gas stream in the proper proportions to obtain the desired benzene partial pressure. The value of the adsorption at 50 Torr of benzene is taken from a plot of the adsorption isotherm.

Examples 1 to 23 relate to the preparation and characterization of the synthetic ultra large pore compositions which are modified by the present invention. Examples 24 to 28 relate to the modification process of the present invention to provide a trivalent element-containing material and a comparison with siliceous materials and trivalent element-containing materials made by directly crystallizing a reaction mixture containing trivalent element.

In the examples metric units and parts by weight are employed unless otherwise indicated.

EXAMPLE 1

One hundred grams of cetyltrimethylammonium (CTMA) hydroxide solution, prepared by contacting a 29 wt. % N,N,N-trimethyl-1-hexadecanaminium chloride solution with a hydroxide-for-halide exchange resin, was combined with 100 grams of an aqueous solution of tetramethylammonium (TMA) silicate (10% silica) with stirring. Twenty-five grams of HiSil, a precipitated hydrated silica containing about 6 wt. % free water and about 4.5 wt. % bound water of hydration and having an ultimate particle size of about 0.02 micron, was added. The resulting mixture was placed in a polypropylene bottle, which was kept in a steam box at 95° C. overnight. The mixture had a composition in terms of moles per mole Al₂ O₃ :

2.7 moles Na₂ O

392 moles SiO₂

35.7 moles (CTMA)₂ O

61.7 moles (TMA)₂ O

6231 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have a surface area of 475 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               8.3                                                                   Cyclohexane                                                                             22.9                                                                  n-Hexane 18.2                                                                  Benzene  21.5                                                           ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 1. In this and the following Figures, it is noted that 10 Angstrom Units d-spacing corresponds to 8.842 degrees 2-theta (Cu K-alpha radiation) and 18 Angstrom Units corresponds to 4.909 degrees.

The product of this example may be characterized as including a very strong relative intensity line at 37.8±2.0 Angstroms d-spacing, and weak lines at 21 6±1.0 and 19.2±1.0 Angstroms. The present ultra-large pore material was demonstrated to be in the product of this example by transmission electron microscopy (TEM), which produced images of a hexagonal arrangement of uniform pores and hexagonal electron diffraction pattern with a d₁₀₀ value of about 39 Angstroms.

EXAMPLE 2

One hundred grams of cetyltrimethylammonium (CTMA) hydroxide solution prepared as in Example 1 was combined with 100 grams of an aqueous solution of tetramethylammonium (TMA) hydroxide (25%) with stirring. Twenty-five grams of HiSil, a precipitated hydrated silica containing about 6 wt. % free water and about 4.5 wt. % bound water of hydration and having an ultimate particle size of about 0.02 micron, was added. The resulting mixture was placed in a static autoclave at 150° C. overnight. The mixture had a composition in terms of moles per mole Al₂ O₃ :

2.7 moles Na₂ O

291 moles SiO₂

35.7 moles (CTMA)₂ O

102 moles (TMA)₂ O

6120 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have a surface area of 993 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               7.1                                                                   Cyclohexane                                                                             47.2                                                                  n-Hexane 36.2                                                                  Benzene  49.5                                                           ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 2. It may be characterized as including a very strong relative intensity line at 39.3±2.0 Angstroms d-spacing, and weak lines at 22.2±1.0 and 19.4±1.0 Angstroms. TEM indicated that the product contained the present ultra-large pore material.

A portion of the above product was then contacted with 100% steam at 1450° F. for two hours. The surface area of the steamed material was measured to be 440 m² /g, indicating that about 45% was retained following severe steaming.

Another portion of the calcined product of this example was contacted with 100% steam at 1250° F. for two hours. The surface area of this material was measured to be 718 m² /g, indicating that 72% was retained after steaming at these conditions.

EXAMPLE 3

Water, cetyltrimethylammonium hydroxide solution prepared as in Example 1, aluminum sulfate, HiSil and an aqueous solution of tetrapropylammonium (TPA) bromide (35%) were combined to produce a mixture having a composition in terms of moles per mole Al₂ O₃ :

0.65 moles Na₂ O

65 moles SiO₂

8.8 moles (CTMA)₂ O

1.22 moles (TPA)₂ O

1336 moles H₂ O

The resulting mixture was placed in a polypropylene bottle, which was kept in a steam box at 95° C. for 192 hours. The sample was then cooled to room temperature and combined with CTMA hydroxide solution prepared as in Example 1 and TMA hydroxide (25% by weight) in the weight ratio of 3 parts mixture, 1 part CTMA hydroxide and 2 parts TMA hydroxide. The combined mixture was then placed in a polypropylene bottle and kept in a steam box at 95° C. overnight. The combined mixture had a composition in terms of moles per mole Al₂ O₃ :

0.65 moles Na₂ O

65 moles SiO₂

15 moles (CTMA)₂ O

1.22 moles (TPA)₂ O

35.6 moles (TMA)₂ O

2927 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have a surface area of 1085 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                         H.sub.2 O      11.5                                                            Cyclohexane    >50                                                             n-Hexane       39.8                                                            Benzene        62                                                              ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 3. The product of this example may be characterized as including a very strong relative intensity line at 38.2±2.0 Angstroms d-spacing, and weak lines at 22.2±1.0 and 19.4±1.0 Angstroms. TEM indicated the product contained the present ultra-large pore material.

EXAMPLE 4

Two hundred grams of cetyltrimethylammonium (CTMA) hydroxide solution prepared as in Example 1 was combined with 2 grams of Catapal alumina (alpha-alumina monohydrate, 74% alumina) and 10o grams of an aqueous solution of tetramethylammonium (TMA) silicate (10% silica) with stirring. Twenty-five grams of HiSil, a precipitated hydrated silica containing about 6 wt. % free water and about 4.5 wt. % bound water of hydration and having an ultimate particle size of about 0.02 micron, was added. The resulting mixture was placed in a static autoclave at 150° C. for 48 hours. The mixture had a composition in terms of moles per mole Al₂ O₃ :

0.23 moles Na₂ O

33 2 moles SiO₂

6.1 moles (CTMA)₂ O

5.2 moles (TMA)₂ O

780 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have a surface area of 1043 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                         H.sub.2 O      6.3                                                             Cyclohexane    >50                                                             n-Hexane       49.1                                                            Benzene        66.7                                                            ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 4. It may be characterized as including a very strong relative intensity line at 40.8±2.0 Angstroms d-spacing, and weak lines at 23.1±1.0 and 20.1±1.0 Angstroms. TEM indicated that the product contained the present ultra-large pore material (see Example 23).

EXAMPLE 5

Two-hundred sixty grams of water was combined with 77 grams of phosphoric acid (85%), 46 grams of Catapal alumina (74% alumina), and 24 grams of pyrrolidine (Pyr) with stirring. This first mixture was placed in a stirred autoclave and heated to 150° C. for six days. The material was filtered, washed and air-dried. Fifty grams of this product was slurried with 200 grams of water and 200 grams of cetyltrimethylammonium hydroxide solution prepared as in Example 1. Four hundred grams of an aqueous solution of tetraethylammonium silicate (10% silica) was then added to form a second mixture which was placed in a polypropylene bottle and kept in a steam box at 95° C. overnight. The first mixture had a composition in terms of moles per mole Al₂ O₃ :

1.0 moles P₂ O₅

0.51 moles (Pyr)₂ O

47.2 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have a surface area of 707 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               33.2                                                                  Cyclohexane                                                                             19.7                                                                  n-Hexane 20.1                                                                  Benzene  23.3                                                           ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 5. It may be characterized as including a very strong relative intensity line at 25.4±1.5 Angstroms d-spacing. TEM indicated the product contained the ultra-large pore material (see Example 23).

EXAMPLE 6

A solution of 1.35 grams of NaAlO₂ (43.5% Al₂ O₃, 30% Na₂ O) dissolved in 45.2 grams of water was mixed with 17.3 grams of NaOH, 125.3 grams of colloidal silica (40%, Ludox HS-40) and 42.6 grams of 40% aqueous solution of tetraethylammonium (TEA) hydroxide. After stirring overnight, the mixture was heated for 7 days in a steam box (95° C.). Following filtration, 151 grams of this solution was mixed with 31 grams of cetyltrimethylammonium hydroxide solution prepared as in Example 1 and stored in the steam box at 95° C. for 13 days. The mixture had the following relative molar composition:

0.25 moles Al₂ O₃

10 moles Na₂ O

36 moles SiO₂

0.95 moles (CTMA)₂ O

2.5 moles (TEA)₂ O

445 moles H₂ O

The resulting solid product was recovered by filtration and washed with water and ethanol. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product composition included 0.14 wt. % Na, 68.5 wt. % SiO₂ and 5.1 wt. % Al₂ O₃, and proved to have a benzene equilibrium adsorption capacity of 58.6 grams/100 grams.

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 6. The product of this example may be characterized as including a very strong relative intensity line at 31.4±1.5 Angstroms d-spacing. TEM indicated that the product contained the present ultra-large pore material.

EXAMPLE 7

A mixture of 300 grams of cetyltrimethylammonium (CTMA) hydroxide solution prepared as in Example 1 and 41 grams of colloidal silica (40%, Ludox HS-40) was heated in a 600 cc autoclave at 150° C. for 48 hours with stirring at 200 rpm. The mixture has a composition in terms of moles per mole SiO₂ :

0.5 mole (CTMA)₂ O

46 5 moles H₂ O

The resulting solid product was recovered by filtration, washed with water, then calcined at 540° C. for 1 hour in nitrogen, followed by 10 hours in air.

The calcined product composition included less than 0.01 wt. % Na, about 98.7 wt. % SiO₂ and about 0.01 wt. % Al₂ O₃, and proved to have a surface area of 896 m² /g. The calcined product had the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               8.4                                                                   Cyclohexane                                                                             49.8                                                                  n-Hexane 42.3                                                                  Benzene  55.7                                                           ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 7. It may be characterized as including a very strong relative intensity line at 40.0±2.0 Angstroms d-spacing and a weak line at 21.2±1.0 Angstroms. TEM indicated that the product of this example contained at least three separate phases, one of which was the present ultra-large pore material.

EXAMPLE 8

A mixture of 150 grams of cetyltrimethylammonium (CTMA) hydroxide solution prepared as in Example 1 and 21 grams of colloidal silica (40%, Ludox HS-40) with an initial pH of 12.64 was heated in a 300 cc autoclave at 150° C. for 48 hours with stirring at 200 rpm. The mixture had a composition in terms of moles per mole SiO₂ :

0.5 mole (CTMA)₂ O

46.5 moles H₂ O

The resulting solid product was recovered by filtration, washed with water, then calcined at 540° C. for 6 hours in air.

The calcined product composition was measured to include 0.01 wt % Na, 93.2 wt. % SiO₂ and 0.016 wt. % Al₂ O₃, and proved to have a surface area of 992 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                         H.sub.2 O      4.6                                                             Cyclohexane    >50                                                             n-Hexane       >50                                                             Benzene        62.7                                                            ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 8. This product may be characterized as including a very strong relative intensity line at 43.6±2.0 Angstroms d-spacing and weak lines at 25.1±1.5 and 21.7±1.0 Angstroms. TEM indicated that the product contained the present ultra-large pore material.

EXAMPLE 9

Sodium aluminate (4.15 g) was added slowly into a solution containing 16 g of myristyltrimethylammonium bromide (C₁₄ TMABr) in 100 g of water. Tetramethylammonium silicate (100 g-10% SiO₂), HiSil (25 g) and tetramethylammonium hydroxide (14.2 g-25% solution) were then added to the mixture. The mixture was crystallized in an autoclave at 120° C. with stirring for 24 hours.

The product was filtered, washed and air dried. Elemental analysis showed the product contained 53.3 wt % SiO₂, 3.2 wt % Al₂ O₃, 15.0 wt % C, 1.88 wt % N, 0.11 wt % Na and 53.5 wt % ash at 1000° C. FIG. 9 shows the X-ray diffraction pattern of the material having been calcined at 540° C. for 1 hour in N₂ and 6 hours in air. The X-ray diffraction pattern includes a very strong relative intensity line at 35.3±2.0 Angstroms d-spacing and weak lines at 20.4±1.0 and 17.7±1.0 Angstroms d-spacing. TEM indicated that the product contained the present ultra-large pore material.

The washed product, having been exchanged with 1N ammonium nitrate solution at room temperature, then calcined, proved to have a surface area of 827 m² /g and the following equilibrium adsorption capacities in g/100 g anhydrous sorbent:

    ______________________________________                                                H.sub.2 O                                                                               30.8                                                                  Cyclohexane                                                                             33.0                                                                  n-Hexane 27.9                                                                  Benzene  40.7                                                           ______________________________________                                    

EXAMPLE 10

Sodium aluminate (8.3 g) was added slowly into a solution containing 184 g of dodecyltrimethylammonium hydroxide (C₁₂ TMAOH, 50%) solution diluted with 480 g of water. UltraSil (50 g) and an aqueous solution of tetramethylammonium silicate (200 g-10% SiO₂) and tetramethylammonium hydroxide (26.38 g-25% solution) were then added to the mixture. The mixture was crystallized in an autoclave at 100° C. with stirring for 24 hours.

The product was filtered, washed and air dried. FIG. 10 shows the X-ray diffraction pattern of the material having been calcined at 540° C. for 1 hour in N₂ and 6 hours in air. The X-ray diffraction pattern includes a very strong relative intensity line at 30.4±1.5 Angstroms d-spacing and weak lines at 17.7±1.0 and 15.3±1.0 Angstroms d-spacing. TEM indicated that the product contained the present ultra-large pore material.

The washed product, having been exchanged with 1N ammonium nitrate solution at room temperature, then calcined, proved to have a surface area of 1078 m² /g and the following equilibrium adsorption capacities in g/100 g anhydrous sorbent:

    ______________________________________                                                H.sub.2 O                                                                               32.6                                                                  Cyclohexane                                                                             38.1                                                                  n-Hexane 33.3                                                                  Benzene  42.9                                                           ______________________________________                                    

EXAMPLE 11

A solution of 4.9 grams of NaAlO₂ (43.5% Al₂ O₃, 30% NaO₂) in 37.5 grams of water was mixed with 46.3 cc of 40% aqueous tetraethylammonium hydroxide solution and 96 grams of colloidal silica (40%, Ludox HS-40). The gel was stirred vigorously for 0.5 hour, mixed with an equal volume (150 ml) of cetyltrimethylammonium hydroxide solution prepared as in Example 1 and reacted at 100° C. for 168 hours. The mixture had the following composition in terms of moles per mole Al₂ O₃ :

1.1 moles Na₂ O

30.6 moles SiO₂

3.0 moles (TEA)₂ O

3.25 moles (CTMA)₂ O

609 moles H₂ O

The resulting solid product was recovered by filtration, washed with water then calcined at 540° C. for 16 hours in air.

The calcined product proved to have a surface area of 1352 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                         H.sub.2 O      23.6                                                            Cyclohexane    >50                                                             n-Hexane       49                                                              Benzene        67.5                                                            ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 11. The product of this example may be characterized as including a very strong relative intensity line at 38.5±2.0 Angstroms d-spacing and a weak line at 20.3±1.0 Angstroms. TEM indicated that the product contained the present ultra-large pore material.

EXAMPLE 12

Two hundred grams of cetyltrimethylammonium (CTMA) hydroxide solution prepared as in Example 1 was combined with 4.15 grams of sodium aluminate and 100 grams of aqueous tetramethylammonium (TMA) silicate solution (10% silica) with stirring. Twenty-five grams of HiSil, a precipitated hydrated silica containing about 6 wt. % free water and about 4.5 wt. % bound water of hydration and having an ultimate particle size of about 0.02 micron, was added. The resulting mixture was placed in a static autoclave at 150° C. for 24 hours. The mixture had a composition in terms of moles per mole Al₂ O₃ :

1.25 moles Na₂ O

27.8 moles SiO₂

5.1 moles (CTMA)₂ O

4.40 moles (TMA)₂ O

650 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air. TEM indicated that this product contained the present ultra-large pore material. The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 12. This pattern can be characterized as including a very strong relative intensity line at 44.2±2.0 Angstroms d-spacing and weak lines at 25.2±1.5 and 22.0±1.0 Angstroms.

The calcined product proved to have a surface area of 932 m² /g and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               39.3                                                                  Cyclohexane                                                                             46.6                                                                  n-Hexane 37.5                                                                  Benzene  50                                                             ______________________________________                                    

The product of this example was then ammonium exchanged with 1N NH₄ NO₃ solution, followed by calcination at 540° C. for 10 hours in air.

EXAMPLE 13

Two hundred grams of cetyltrimethylammonium (CTMA) hydroxide solution prepared as in Example 1 was combined with 4.15 grams of sodium aluminate and 100 grams of aqueous tetramethylammonium (TMA) silicate solution (10% silica) with stirring. Twenty-five grams of HiSil, a precipitated hydrated silica containing about 6 wt. % free water and about 4.5 wt. % bound water of hydration and having an ultimate particle size of about 0.02 micron, was added. The resulting mixture was placed in a steam box at 100° C. for 48 hours. The mixture had a composition in terms of moles per mole Al₂ O₃ :

1.25 moles Na₂ O

27.8 moles SiO₂

5.1 moles (CTMA)₂ O

4.4 moles (TMA)₂ O

650 moles H₂ O

The resulting solid product was recovered by filtration and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                         H.sub.2 O      35.2                                                            Cyclohexane    >50                                                             n-Hexane       40.8                                                            Benzene        53.5                                                            ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 13. This product may be characterized as including a very strong relative intensity line at 39.1±2.0 Angstroms d-spacing and weak lines at 22.4±1.0 and 19.4±1.0 Angstroms. TEM indicated that this product contained the present ultra-large pore material.

The product of this example was then ammonium exchanged with 1N NH₄ NO₃ solution, followed by calcination at 540° C. for 10 hours in air.

EXAMPLE 14

A mixture of 125 grams of 29% CTMA chloride aqueous solution, 200 grams of water, 3 grams of sodium aluminate (in 50 grams H₂ O), 65 grams of Ultrasil, amorphous precipitated silica available from PQ Corporation, and 21 grams NaOH (in 50 grams H₂ O) was stirred thoroughly and crystallized at 150° C. for 168 hours. The reaction mixture had the following relative molar composition in terms of moles per mole silica:

0.10 moles (CTMA)₂ O

21.89 moles H₂ O

0.036 moles NaAlO₂

0.53 moles NaOH

The solid product was isolated by filtration, washed with water, dried for 16 hours at room temperature and calcined at 540° C. for 10 hours in air.

The calcined product proved to have a surface area of 840 m² /g, and the following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               15.2                                                                  Cyclohexane                                                                             42.0                                                                  n-Hexane 26.5                                                                  Benzene  62                                                             ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this Example, shown in FIG. 14, may be characterized as including a very strong relative intensity line at 40.5±2.0 Angstroms d-spacing. TEM indicated that the product contained the present ultra-large pore material.

EXAMPLE 15

For comparison purposes, a commercially prepared ultra-stable zeolite Y was obtained. It had a benzene equilibrium adsorption capacity of 20.7 grams/100 grams. Its X-ray diffraction pattern had all the lines of zeolite Y with its highest value peak at about 14.0 Angstroms d-spacing.

EXAMPLE 16

To make the primary template mixture for this example, 240 grams of water was added to a 92 gram solution of 50% dodecyltrimethylammonium hydroxide, 36% isopropyl alcohol and 14% water such that the mole ratio of Solvent/R_(2/f) O was 155. The mole ratio of H₂ O/R_(2/f) O in this mixture was 149 and the IPA/R_(2/f) O mole ratio was 6. To the primary template mixture was added 4.15 grams of sodium aluminate, 25 grams of HiSil, grams of aqueous tetramethylammonium silicate solution (10% SiO₂) and 13.2 grams of 25% aqueous tetramethylammonium hydroxide solution. The mole ratio of R_(2/f) O/(SiO₂ +Al₂ O₃) was 0.28 for the mixture.

This mixture was stirred at 25° C. for 1 hour. The resulting mixture was then placed in an autoclave at 100° C. and stirred at 100 rpm for 24 hours. The mixture in the autoclave had the following relative molar composition in terms of moles per mole SiO₂ :

0.05 mole Na₂ O

0.036 mole Al₂ O₃

0.18 mole (C₁₂ TMA)₂ O

0.12 mole (TMA)₂ O

36.0 moles H₂ O

1.0 mole IPA

The resulting solid product was recovered by filtration, washed with water and dried in air at ambient temperature. The product was then calcined at 540° C. for 1 hour in nitrogen, followed by 6 hours in air.

The calcined product proved to have a surface area of 1223 m² /g following equilibrium adsorption capacities in grams/100 grams:

    ______________________________________                                                H.sub.2 O                                                                               25.5                                                                  Cyclohexane                                                                             41.1                                                                  n-Hexane 35.1                                                                  Benzene  51                                                             ______________________________________                                    

The X-ray diffraction pattern of the calcined product of this example is shown in FIG. 15. This product may be characterized as including a very strong relative intensity line at 30.8±1.5 Angstroms d-spacing and weak lines at 17.9±1.0 and 15.5±1.0 Angstroms. TEM indicated this product to contain the present ultra-large pore material.

EXAMPLE 17

A 50.75 gram quantity of decyltrimethylammonium hydroxide (prepared by contacting a ca. 29 wt. % solution of decyltrimethylammonium bromide with a hydroxide-for-halide exchange resin) was combined with 8.75 grams of tetraethylorthosilicate. The mixture was stirred for about 1 hour and then transferred to a polypropylene jar which was then placed in a steambox for about 24 hours. The mixture had a composition in terms of moles per mole SiO₂ :

0.81 mole (C₁₀ TMA)₂ O

47.6 moles H₂ O

The resulting solid product was filtered and washed several times with warm (60°-70° C.) distilled water and with acetone. The final product was calcined to 538° C. in N₂ /air mixture and then held in air for about 8 hours.

The calcined product proved to have a surface area of 915 m² /g and an equilibrium benzene adsorption capacity of 35 grams/100 grams. Argon physisorption data indicated an argon uptake of 0.34 cc/gram, and a pore size of 15 Angstroms.

The X-ray diffraction pattern of the calcined product of this example may be characterized as including a very strong relative intensity line at 27.5±1.5 Angstroms d-spacing and weak lines at 15.8±1.0 and 13.7±1.0 Angstroms. TEM indicated that the product of this example contained the present ultra-large pore material.

EXAMPLE 18

To eighty grams of cetyltrimethylammonium hydroxide (CTMAOH) solution prepared as in Example 1 was added 1.65 grams of NaAlO₂. The mixture was stirred at room temperature until the NaAlO₂ was dissolved. To this solution was added 40 grams of aqueous tetramethylammonium (TMA) silicate solution (10 wt. % SiO₂), 10 grams of HiSil, 200 grams of water and 70 grams of 1,3,5-trimethylbenzene (mesitylene). The resulting mixture was stirred at room temperature for several minutes. The gel was then loaded into a 600 cc autoclave and heated at 105° C. for sixty-eight hours with stirring at 150 rpm. The mixture had a composition in terms of moles per mole Al₂ O₃ :

1.25 moles Na₂ O

27.8 moles SiO₂

5.1 moles (CTMA)₂ O

2.24 moles (TMA)₂ O

2256 moles H₂ O

80.53 moles 1,3,5-trimethylbenzene

The resulting product was filtered and washed several times with warm (60°-70° C.) distilled water and with acetone. The final product was calcined to 538° C. in N₂ /air mixture and then held in air for about 10 hours.

The calcined product proved to have an equilbrium benzene adsorption capacity of >25 grams/100 grams.

The X-ray diffraction pattern of the calcined product of this example may be characterized as including a broad, very strong relative intensity line at about 102 Angstroms d-spacing, but accurate positions of lines in the extreme low angle region of the X-ray diffraction pattern are very difficult to determine with conventional X-ray diffractometers. Furthermore, finer collimating slits were required to resolve a peak at this low 2-theta angle. The slits used in this example, starting at the X-ray tube, were 0.1, 0.3, 0.5 and 0.2 mm, respectively. TEM indicated that the product of this example contained several materials with different d₁₀₀ values as observed in their electron diffraction patterns. These materials were found to possess d₁₀₀ values between about 85 Angstroms d-spacing and about 120 Angstroms d-spacing.

EXAMPLE 19

To eighty grams of cetyltrimethylammonium hydroxide (CTMAOH) solution prepared as in Example 1 was added 1.65 grams of NaAlO₂. The mixture was stirred at room temperature until the NaAlO₂ was dissolved. To this solution was added 40 grams of aqueous tetramethylammonium (TMA) silicate solution (10 wt. % SiO₂), 10 grams of HiSil, 200 grams of water and 120 grams of 1,3,5-trimethylbenzene (mesitylene). The resulting mixture was stirred at room temperature for several minutes. The gel was then loaded into a 600 cc autoclave and heated at 105° C. for ninety hours with stirring at 150 rpm. The mixture had a composition in terms of moles per mole Al₂ O₃ :

1.25 moles Na₂ O

27.8 moles SiO₂

5.1 moles (CTMA)₂ O

2.24 moles (TMA)₂ O

2256 moles H₂ O

132.7 moles 1,3,5-trimethylbenzene

The resulting product was filtered and washed several times with warm (60°-70° C.) distilled water and with acetone. The final product was calcined to 538° C. in N₂ /air mixture and then held in air for about 10 hours.

The calcined product proved to have a surface area of 915 m² g and an equilbrium benzene adsorption capacity of >25 grams/100 grams. Argon physisorption data indicated an argon uptake of 0.95 cc/gram, and a pore size centered on 78 Angstroms (Dollimore-Heal Method, see Example 22(b)), but running from 70 to greater than 105 Angstoms.

The X-ray diffraction pattern of the calcined product of this example may be characterized as having only enhanced scattered intensity in the very low angle region of the X-ray diffraction, where intensity from the transmitted incident X-ray beam is usually observed. However, TEM indicated that the product of this example contained several materials with different d₁₀₀ values as observed in their electron diffraction patterns. These materials were found to possess d₁₀₀ values between about 85 Angstroms d-spacing and about 110 Angstroms d-spacing.

EXAMPLE 20

To eighty grams of cetyltrimethylammonium hydroxide (CTMAOH) solution prepared as in Example 1 was added 1.65 grams of NaAlO₂. The mixture was stirred at room temperature until the NaAlO₂ was dissolved. To this solution was added 40 grams of aqueous tetramethylammonium (TMA) silicate solution (10 wt. % SiO₂), 10 grams of HiSil, and 18 grams of 1,3,5-trimethylbenzene (mesitylene). The resulting mixture was stirred at room temperature for several minutes. The gel was then loaded into a 300 cc autoclave and heated at 105° C. for four hours with stirring at 150 rpm. The mixture had a composition in terms of moles per mole Al₂ O₃ :

25 moles Na₂ O

27.8 moles SiO₂

5.1 moles (CTMA)₂ O

2.24 moles (TMA)₂ O

650 moles H₂ O

19.9 moles 1,3,5-trimethylbenzene

The resulting product was filtered and washed several times with warm (60°-70° C.) distilled water and with acetone. The final product was calcined to 538° C. in N₂ /air mixture and then held in air for about 8 hours.

The calcined product proved to have a surface area of 975 m² /g and an equilbrium benzene adsorption capacity of >40 grams/100 grams. Argon physisorption data indicated an argon uptake of 0.97 cc/gram, and a pore size of 63 Angstroms (Dollimore-Heal Method, see Example 22(b)), with the peak occurring at P/P_(o) =0.65.

The X-ray diffraction pattern of the calcined product of this example may be characterized as including a very strong relative intensity line at 63±5 Angstroms d-spacing and weak lines at 36.4±2.0, 31.3±1.5 Angstroms and 23.8±1.0 Angstroms d-spacing. TEM indicated that the product of this example contained the present ultra-large pore material.

EXAMPLE 21

For catalytic evaluation of the present invention, final products from Examples 1 through 15 were evaluated for dealkylation of tri-tert-butylbenzene (TBB) to di-tert butylbenzene. The present evaluation was conducted under one or both of two sets of conditions: (i) at a temperature of 225° C., weight hourly space velocity of 100 hr⁻¹ or (ii) at a temperature of 200° C., weight hourly space velocity of 200 hr⁻¹. Pressure was atmospheric. The feed was composed of 6.3/93.7 TTBB/toluene. Conversion was measured at 30 minutes on stream.

The results were as follows:

    ______________________________________                                         Catalyst of                                                                               Conversion, wt. %                                                   Example    225° C./100 hr.sup.-1                                                                200° C./200 hr.sup.-1                           ______________________________________                                         1          0            --                                                     2          6.2          --                                                     3          53.9         --                                                     4          10.4         --                                                     5          68.9         --                                                     6          100.0        --                                                     7          93.4         66.0                                                   8          5.3          --                                                     9          --           61.2                                                   10         --           58.9                                                   11         86.3         --                                                     12         96.7         --                                                     13         92.8         --                                                     14         --           37.7                                                   15         12.0         0                                                      ______________________________________                                    

EXAMPLE 22(a) Argon Physisorption For Pore Systems Up to About 60 Angstroms Diameter

To determine the pore diameters of the products of this invention with pores up to about 60 Angstroms in diameter, 0.2 gram samples of the products of Examples 1 through 17 were placed in glass sample tubes and attached to a physisorption apparatus as described in U.S. Pat. No. 4,762,010, which is incorporated herein by reference.

The samples were heated to 300° C. for 3 hours in vacuo to remove adsorbed water. Thereafter, the samples were cooled to 87° K. by immersion of the sample tubes in liquid argon. Metered amounts of gaseous argon were then admitted to the samples in stepwise manner as described in U.S. Pat. No. 4,762,010, column 20. From the amount of argon admitted to the samples and the amount of argon left in the gas space above the samples, the amount of argon adsorbed can be calculated. For this calculation, the ideal gas law and the calibrated sample volumes were used. (See also S. J. Gregg et al., Adsorption, Surface Area and Porosity, 2nd ed., Academic Press, 1982). In each instance, a graph of the amount adsorbed versus the relative pressure above the sample, at equilibrium, constitutes the adsorption isotherm as shown in FIG. 16 for the Example 4 product sample. It is common to use relative pressures which are obtained by forming the ratio of the equilibrium pressure and the vapor pressure P_(o) of the adsorbate at the temperature where the isotherm is measured. Sufficiently small amounts of argon were admitted in each step to generate 168 data points in the relative pressure range from 0 to 0.6. At least about 100 points are required to define the isotherm with sufficient detail.

The step (inflection) in the isotherm, in this case (Example 4 product) at about P/P_(o) =0.4, indicates filling of a pore system. The size of the step indicates the amount adsorbed, whereas the position of the step in terms of P/P_(o) reflects the size of the pores in which the adsorption takes place. Larger pores are filled at higher P/P_(o). In order to better locate the position of the step in the isotherm, the derivative with respect to log (P/P_(o)) is formed. This is shown in FIG. 17. Also shown in FIG. 17 are data obtained in an identical fashion for a crystalline material from U.S. Pat. No. 4,880,611 and several other crystal materials. There is further provided a physical scale on the axis which converts the position of an adsorption peak in terms of log (P/P_(o)) to the physical pore diameter in Angstroms. This conversion was obtained by using the following formula: ##EQU1## wherein d=pore diameter in nanometers, K=32.17, S=0.2446, L=d+0.19, and D=0.57.

This formula is derived from the method of Horvath and Kawazoe (G. Horvath et al., J. Chem. Eng. Japan, 16 (6) 470(1983)). The constants required for the implementation of this formula were determined from a measured isotherm of ALPO-5 and its known pore size. This method is particularly useful for microporous materials having pores of up to about 60 Angstroms in diameter.

As is indicated in FIG. 17, the pore size of the material of Example 4 is 39.6 Angstroms with the peak occurring at log (P/P_(o))=-0.4 or P/P_(o) =0.4, while the pore size of the material from U.S. Pat. No. 4,880,611 is 12 Angstroms or P/P_(o) =0.02. In the other materials, a peak is observed at P/P_(o) =0.015 which is denoted by an asterisk in FIG. 17. This peak reflects adsorption on the walls of the pores and is not otherwise indicative of the size of the pores of a given material. A value of P/P_(o) of 0.03 corresponds to 13 Angstroms pore size.

The results of this procedure for the samples from Examples 1 through 17 are tabulated below. The samples from Examples 10, 13 and 16 gave two separate peaks, believed to be the result of two separate ultra-large pore phases in the products.

    ______________________________________                                         Examples   Pore Diameter, Angstroms                                            ______________________________________                                         1          32.2                                                                2          35.4                                                                3          42.5                                                                4          39.6                                                                5          16.9                                                                6          27.3                                                                7          36.6                                                                8          42.6                                                                9          28.3                                                                10         22.8,           30.8                                                11         36.8                                                                12         36.1                                                                13         35.0,           42.1                                                14         40.0                                                                15         8.3                                                                 16         22.4,           30.4                                                17         15.0                                                                ______________________________________                                    

EXAMPLE 22(b) Argon Physisorption For Pore Systems Over About 60 Angstrom Units Diameter

In the pore regime above 60 Angstrom Units diameter, the Kelvin equation can be applied. It is usually given as: ##EQU2## where: γ=surface tension of sorbate

V=molar volume of sorbate

Θ=contact angle (usually taken for practical reasons to be 0)

R=gas constant

T=absolute temperature

r_(k) =capillary condensate (pore) radius

P/P_(o) =relative pressure (taken from the physisorption isotherm)

The Kelvin equation treats adsorption in pore systems as a capillary condensation phenomenon and relates the pressure at which adsorption takes place to the pore diameter through the surface tension and contact angle of the adsorbate (in this case, argon). The principles upon which the Kelvin equation are based are valid for pores in the size range 50 to 1000 Angstrom Units diameter. Below this range the equation no longer reflects physical reality, since true capillary condensation cannot occur in smaller pores; above this range the logarithmic nature of the equation precludes obtaining sufficient accuracy for pore size determination.

The particular implementation of the Kelvin equation often chosen for measurement of pore size is that reported by Dollimore and Heal (D. Dollimore and G. R. Heal, J. Applied Chem., 14, 108 (1964)). This method corrects for the effects of the surface layer of adsorbate on the pore wall, of which the Kelvin equation proper does not take account, and thus provides a more accurate measurement of pore diameter. While the method of Dollimore and Heal was derived for use on desorption isotherms, it can be applied equally well to adsorption isotherms by simply inverting the data set.

The products of Examples 18 and 19 were subjected to the Dollimore and Heal Method for argon physisorption data, as indicated.

EXAMPLE 23 Transmission Electron Microscopy

To further illustrate the nature of the hexagonal crystalline product of this invention, samples of the products from Examples 1-4, and 16 through 20 were studied by transmission electron microscopy (TEM) as noted above. TEM is a technique used to reveal the microscopic structure of materials, including crystalline materials.

In order to illuminate the microstructure of materials, samples must be thin enough for an electron beam to pass through them, generally about 500-1000 Angstrom Units thick. The crystal morphology of the present materials usually required that they be prepared for study by ultramicrotomy. While time consuming, this technique of sample preparation is quite familiar to those skilled in the art of electron microscopy. The materials are embedded in a resin, in this case a commercially available low viscosity acrylic resin L.R. WHITE (hard), which is then cured at about 80° C. for about 11/2 hours. Thin sections of the block are cut on an ultramicrotome using a diamond knife and sections in the thickness range 500-1000 Angstrom Units are collected on fine mesh electron microscope support grids. For these materials, an LKB model microtome with a 45° C. diamond knife edge was used; the support grids were 400 mesh copper grids. After evaporation of a thin carbon coating on the sample to prevent charging in the microscope (light gray color on a white sheet of paper next to the sample in the evaporator), the samples are ready for examination in the TEM.

A simpler specimen preparation technique can be used with most synthesis preparations if mere verification of the presence of the material of the invention is desired. This involves deposition of a dispersion of the material on a carbon-coated lacy Formvar electron microscope support after grinding and sonication in propanol. Fragments or regions sufficiently thin to obtain electron diffraction patterns and lattice images can normally be found near the edges of the crystals.

High resolution TEM micrographs show projections of structure along the direction that the sample is viewed. For this reason, it is necessary to have a sample in specific orientations to see certain details of the microstructure of the material. For crystalline materials, these orientations are most easily chosen by observing the electron diffraction pattern (EDP) that is produced simultaneously with the electron microscope image. Such EDP's are readily produced on modern TEM instruments using, e.g. the selected area field limiting aperture technique familiar to those skilled in the art of electron microscopy. When an EDP with the desired arrangement of diffraction spots is observed, the corresponding image of the crystal giving that EDP will reveal details of the microstructure along the direction of projection indicated by the EDP. In this way, different projections of a crystal's structure can be observed and identified using TEM.

In order to observe the salient features of the crystalline product of the present invention, it is necessary to view the material in an orientation wherein the corresponding EDP gives a hexagonal arrangement of diffraction spots from a single individual crystal. If multiple crystals are present within the field limiting aperture, overlapping diffraction patterns will occur that can be quite difficult to interpret. An example of a hexagonal pattern from an individual crystal from the product in Example 4 is shown in FIG. 17. The number of diffraction spots observed depends to a degree upon the regularity of the crystalline arrangement in the material, among other things. At the very least, however, the inner ring of bright spots should be observed to obtain a good image. Individual crystals can be manipulated by specimen tilt adjustments on the TEM until this orientation is achieved. More often, it is easier to take advantage of the fact that the specimen contains many randomly oriented crystals and to simply search through the sample until a crystal giving the desired EDP (and hence orientation) is located. This latter technique was used to produce the electron micrographs discussed below.

Microtomed samples of materials from the Examples 1-4 and 16-20 were examined by the techniques described above in a JEOL 200 CX transmission electron microscope operated at 200,000 volts with an effective 2 Angstrom Units objective aperture in place. The instrument has a point-to-point resolution of 4.5 Angstrom Units. Other experimental arrangements familiar to one skilled in the art of high resolution (phase contrast) TEM could be used to produce equivalent images provided care is taken to keep the objective lens on the underfocus side of the minimum contrast lens current setting. FIG. 18 is an electron micrograph from a microtomed thin section of the crystalline product from Example 4. This micrograph shows a reasonably regular array of large channels in a hexagonal arrangement. The repeat distance between the channels is about 45 Angstrom units, which is consistent with the position of the first peak in the X-ray diffraction pattern (41 Angstroms/√3/2) of this material. Since the channels must have walls between them, this observation is also consistent with the estimated pore size of about 39.6 Angstrom Units calculated from Argon physisorption measurements of this material in Example 16.

FIG. 19 is an electron micrograph from a microtomed thin section of the crystalline product from Example 5. This micrograph shows a reasonably regular array of somewhat smaller channels in a hexagonal arrangement. The repeat distance between the channels is about 30 Angstrom Units, which is consistent with the position of the first peak in the X-ray diffraction pattern (2.5 Angstroms/√3/2) of this material. The smaller pore size of this material was also verified by Argon physisorption measurements reported in Example 21(a), where a value of 16.9 Angstrom Units was calculated for the material in Example 5.

FIG. 20 is an electron micrograph from a microtomed thin section of the crystalline product from Example 18. The channels in this image are quite large and rather irregular, but the characteristic hexagonal arrangement of the material of the present invention is evident.

EXAMPLE 24 Preparation of Siliceous MCM-41

A mixture of 300 g of 29% cetyltrimethylammonium (CTMA) hydroxide and 41 g of Ludox HS-40 was reacted in a stirred autoclave at 150° C. for 48 hours. The resulting solid was isolated by filtration, washed with water and dried at 100°-110° C. The organic component was removed by calcination at 540° C. and the resultant solid exhibited an X-ray diffraction pattern consistent with the ultra-large pore material with CuKα lines at 2.3 and 4.2 degrees.

EXAMPLE 25 Modification of Siliceous MCM-41 with Sodium Aluminate

3 g of the product of Example 24 were stirred for 20 hours in a solution of 5 g of sodium aluminate in 20 g of water. The solid was filtered, washed with water and dried at 100° C. for 2 hours. It was then exchanged three times with ammonium nitrate at pH=8. After calcination at 540° C. it was tested for tri-t-butylbenzene conversion. A sample was steamed at 677° C. with 100% steam for two hours and tested at 225° C., 1 atmosphere, 100 WHSV for 30 minutes on stream. The results for TTTB conversion are presented in Table I below.

EXAMPLE 26 Preparation of Siliceous MCM-41

A mixture of 300 g of 29% cetyltrimethylammonium (CTMA) hydroxide and 21 g of Ludox HS-40 with pH adjusted to 12.9 was reacted in a stirred autoclave at 150° C. for 48 hours. The resulting solid was isolated by filtration, washed with water and dried at 100°-110° C. The organic component was removed by calcination at 540° C. and the resultant solid exhibited a powder pattern consistent with the ultra-large pore material with CuKα lines at 2.1 and 3.6-4.2 degrees.

EXAMPLE 27 Modification of Siliceous MCM-41 with Sodium Aluminate

5.17 g of the product of Example 26 were stirred for 5 hours in a solution of 5 g of sodium aluminate in 50 g of water. The solid was filtered, washed with water and dried at 100° C. for 2 hours. It was then exchanged three times with ammonium nitrate at pH=8. After calcination at 540° C. it was tested for tri-t-butylbenzene conversion. A sample was steamed at 677° C. with 100% steam for two hours and tested as in Example 25. The results are set out in Table I below.

EXAMPLE 28 (COMPARATIVE) Preparation of Al-Containing MCM-41 from Aluminosilicate Gel

3.6 g of sodium aluminate were dissolved in 10 g of water and mixed with 500 g of 29% cetyltrimethylammonium hydroxide and 60 g of Ludox HS-40. It was reacted in a one liter autoclave at 150° C. for 44 hours with stirring at 200 rpm. It was isolated, worked up and tested as in Example 25. The results are set out in Table I below.

                  TABLE I                                                          ______________________________________                                         Catalytic Activity - % Conversion of TTBB* By MCM-41                           Materials Before and After Steaming                                            (2 Hours, 677° C., 100% Steam)                                                       % TTBB Conversion                                                 Product of     Before Steaming                                                                             After Steaming                                     ______________________________________                                         Example 24 (Siliceous)                                                                        5.9          0.0                                                Example 25     93.5         76.9                                               Example 27     97.3         87.9                                               Example 28     88.4         49.9                                               ______________________________________                                    

The results show that the present invention provides a means for modifying synthetic ultra large pore compositions by treatment with oxides of trivalent elements to provide a catalyst of enhanced activity. The method of the present invention provides a catalyst exhibiting significantly more activity after steaming than synthetic ultra-large pore compositions prepared by crystallizing an aluminosilicate gel or siliceous compositions. 

What is claimed is:
 1. A method for modifying a composition of matter comprising an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than 18 Angstrom Units and having a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 6.7 kPa (50 torr) and 25° C., comprising:contacting with a treatment composition comprising an inorganic oxide of a trivalent element X or a precursor of said inorganic oxide; said contacting occurring under sufficient conditions so that the trivalent element X is incorporated in said crystalline phase material.
 2. The method of claim 1 wherein the composition of matter comprises an inorganic, porous crystalline phase material having a hexagonal arrangement of uniformly-sized pores at least about 15 Angstroms in diameter and exhibiting, after calcination, a hexagonal electron diffraction pattern that can be indexed with a d₁₀₀ value greater than 18 Angstrom Units.
 3. The method of claim 1 wherein the composition of matter has a composition expressed as follows:

    M.sub.n/q (W.sub.a X.sub.b Y.sub.c Z.sub.d O.sub.h)

wherein M is one or more ions; n is the charge of the composition excluding M expressed as oxides; q is the weighted molar average valence of M; n/q is the number of moles or mole fraction of M; W is one or more divalent elements; X is one or more trivalent elements; Y is one or more tetravalent elements; Z is one or more pentavalent elements; a, b, c, and d are mole fractions of W, X, Y, and Z, respectively; h is a number of from 1 to 2.45; and (a+b+c+d)=1.
 4. The method of claim 1 wherein the composition of matter has a composition on an anhydrous basis, expressed as follows:

    rRM.sub.n/q (W.sub.a X.sub.b Y.sub.c Z.sub.d O.sub.h)

wherein R is the total organic material not included in M; r is the number of moles or mole fraction of R; M is one or more ions; n is the charge of the composition excluding M expressed as oxides; q is the weighted molar average valence of M; n/q is the mumber of moles or mole fraction of M; W is one or more divalent elements; X is one or more trivalent elements; Y is one or more tetravalent elements; Z is one or more pentavalent elements; a, b, c, and d are mole fractions of W, X, Y, and Z, respectively; h is a number of from 1 to 2.5; and (a+b+c+d)=1, wherein, when treated under conditions sufficient to remove R, said crystalline phase gives an X-ray diffraction pattern with at least one peak at a position greater than about 18 Angstrom Units d-spacing and exhibits a benzene adsorption capacity of greater than about 15 grams benzene per 100 grams anhydrous crystal at 50 torr and 25° C.
 5. The method of claim 1 wherein the composition of matter comprises an inorganic, non-pillared crystalline phase giving an X-ray diffraction pattern following calcination with at least two peaks at positions greater than about 10 Angstrom Units d-spacing, and no peaks at positions less than about 10 Angstrom Units d-spacing with relative intensity greater than about 20% of the strongest peak.
 6. The method of claim 1 wherein the inorganic oxide of a trivalent element X is an inorganic oxide of a trivalent element selected from the group consisting of aluminum, boron, iron, gallium and indium.
 7. The method of claim 1 wherein the inorganic oxide of a trivalent element X is an anion.
 8. The method of claim 1 wherein the inorganic oxide of a trivalent element X is AlO₂.
 9. The method of claim 1 wherein the inorganic oxide of a trivalent element X is an inorganic oxide of aluminum.
 10. The method of claim 1 wherein the inorganic oxide of a trivalent element X is an inorganic oxide of boron.
 11. The method of claim 1 wherein the inorganic oxide of a trivalent element X is an inorganic oxide of gallium.
 12. The method of claim 1 wherein said contacting is carried out with an aqueous solution of said inorganic oxide of a trivalent element X.
 13. The method of claim 3 wherein a, b, and d are about
 0. 14. The method of claim 1 wherein said modifying provides a catalyst of increased catalytic activity.
 15. The crystalline material modified by the method of claim
 1. 16. The crystalline material modified by the method of claim
 8. 